Organic light-emitting materials containing cyano-substituted ligand

ABSTRACT

An organic light-emitting material containing cyano-substituted ligand is disclosed. The organic light-emitting material is a metal complex containing a cyano-substituted ligand, which can be used as a light-emitting material in a light-emitting layer of an organic electroluminescent device. These new complexes can provide better device performance, e.g., narrower full width at half maximum, lower voltage values, and higher quantum efficiency, and the like. An electroluminescent device and a compound formulation containing the metal complex, and a compound capable of being used to prepare the metal complex are also disclosed.

This application is a continuation application of U.S. application Ser. No. 16/750,282 titled “ORGANIC LIGHT-EMITTING MATERIALS CONTAINING A CYANO-SUBSTITUTED LIGAND” filed on Jan. 23, 2020, which claims priority to Chinese Patent Application No. 201910077079.0 filed on Feb. 1, 2019, and the entirety of each of which is incorporated herein by reference.

TECHNICAL FIELD

The present disclosure relates to a compound for using in an organic electronic device, such as an organic light-emitting device. In particular, it relates to a metal complex containing a cyano-substituted ligand, and an electroluminescent device and a compound formulation containing the metal complex.

BACKGROUND

Organic electronic devices include, but are not limited to, the following types: organic light-emitting diodes (OLEDs), organic field-effect transistors (O-FETs), organic light-emitting transistors (OLETs), organic photovoltaic devices (OPVs), dye-sensitized solar cells (DSSCs), organic optical detectors, organic photoreceptors, organic field-quench devices (OFQDs), light-emitting electrochemical cells (LECs), organic laser diodes and organic plasmon emitting devices.

In 1987, Tang and Van Slyke of Eastman Kodak reported a bilayer organic electroluminescent device, which comprises an arylamine hole transporting layer and a tris-8-hydroxyquinolato-aluminum layer as the electron and emitting layer (Applied Physics Letters, 1987, 51 (12): 913-915). Once a bias is applied to the device, green light was emitted from the device. The present disclosure laid the foundation for the development of modem organic light-emitting diodes (OLEDs). State-of-the-art OLEDs may comprise multiple layers such as charge injection and transporting layers, charge and exciton blocking layers, and one or multiple emissive layers between the cathode and anode. Since OLED is a self-emitting solid state device, it offers tremendous potential for display and lighting applications. In addition, the inherent properties of organic materials, such as their flexibility, may make them well suited for particular applications such as fabrication on flexible substrates.

OLED can be categorized as three different types according to its emitting mechanism. The OLED invented by Tang and van Slyke is a fluorescent OLED. It only utilizes singlet emission. The triplets generated in the device are wasted through nonradiative decay channels. Therefore, the internal quantum efficiency (IQE) of a fluorescent OLED is only 25%. This limitation hindered the commercialization of OLED. In 1997, Forrest and Thompson reported phosphorescent OLED, which uses triplet emission from heave metal containing complexes as the emitter. As a result, both singlet and triplets can be harvested, achieving 100% IQE. The discovery and development of phosphorescent OLED contributed directly to the commercialization of active-matrix OLED (AMOLED) due to its high efficiency. Recently, Adachi achieved high efficiency through thermally activated delayed fluorescence (TADF) of organic compounds. These emitters have small singlet-triplet gap that makes the transition from triplet back to singlet possible. In the TADF device, the triplet excitons can go through reverse intersystem crossing to generate singlet excitons, resulting in high IQE.

OLEDs can also be classified as small molecule and polymer OLEDs according to the forms of the materials used. Small molecule refers to any organic or organometallic material that is not a polymer. The molecular weight of a small molecule can be large as long as it has well defined structure. Dendrimers with well-defined structures are considered as small molecules.

Polymer OLEDs include conjugated polymers and non-conjugated polymers with pendant emitting groups. Small molecule OLED can become a polymer OLED if post polymerization occurred during the fabrication process.

There are various methods for OLED fabrication. Small molecule OLEDs are generally fabricated by vacuum thermal evaporation. Polymer OLEDs are fabricated by solution process such as spin-coating, inkjet printing, and slit printing. If the material can be dissolved or dispersed in a solvent, the small molecule OLED can also be produced by solution process.

The emitting color of an OLED can be achieved by emitter structural design. An OLED may comprise one emitting layer or a plurality of emitting layers to achieve desired spectrum. In the case of green, yellow, and red OLEDs, phosphorescent emitters have successfully reached commercialization. Blue phosphorescent device still suffers from non-saturated blue color, short device lifetime, and high operating voltage. Commercial full-color OLED displays normally adopt a hybrid strategy, using fluorescent blue and phosphorescent yellow, or red and green. At present, efficiency roll-off of phosphorescent OLEDs at high brightness remains a problem. In addition, it is desirable to have more saturated emitting color, higher efficiency, and longer device lifetime.

Cyano substitution is not often introduced into phosphorescent metal complexes, such as iridium complexes. US20140252333A1 discloses a series of iridium complexes substituted with cyano-phenyl, and as a result, the effect brought by the cyano group is not clearly indicated. In addition, since the cyano group is a very electron-withdrawing substituent, it is also used to blue-shift the emission spectrum of phosphorescent metal complexes, such as disclosed in US20040121184A1.

SUMMARY

The present disclosure aims to provide a series of technical solutions to solve at least part of the above problems.

One object of the present disclosure is to provide a metal complex comprising a ligand La represented by Formula 1:

-   -   wherein, Cy is a substituted or unsubstituted aryl or heteroaryl         group having 5 to 24 ring atoms;     -   wherein, Cy is connected to a metal through a metal-carbon bond         or a metal-nitrogen bond;     -   wherein, X₁ to X₄ are each independently selected from C,         CR_(x1) or N, and at least one of X₁ to X₄ is C and connected to         Cy; when more than one of X₁ to X₄ is CR_(x1), the R_(x1) may be         the same or different;     -   wherein, X₅ to X₈ are each independently selected from CR_(x2)         or N; when more than one of X₅ to X₈ is CR_(x2), the R_(x2) may         be the same or different;     -   wherein, X is selected from the group consisting of O, S, Se,         NR_(x3), CR_(x4)R_(x5) and SiR_(x6)R_(x7);     -   wherein, R_(x1), R_(x2), R_(x3), R_(x4), R_(x5), R_(x6) and         R_(x7) are each independently selected from the group consisting         of hydrogen, deuterium, halogen, a substituted or unsubstituted         alkyl group having 1-20 carbon atoms, a substituted or         unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a         substituted or unsubstituted heteroalkyl group having 1-20         carbon atoms, a substituted or unsubstituted arylalkyl group         having 7-30 carbon atoms, a substituted or unsubstituted alkoxy         group having 1-20 carbon atoms, a substituted or unsubstituted         aryloxy group having 6-30 carbon atoms, a substituted or         unsubstituted alkenyl group having 2-20 carbon atoms, a         substituted or unsubstituted aryl group having 6-30 carbon         atoms, a substituted or unsubstituted heteroaryl group having         3-30 carbon atoms, a substituted or unsubstituted alkylsilyl         group having 3-20 carbon atoms, a substituted or unsubstituted         arylsilyl group having 6-20 carbon atoms, a substituted or         unsubstituted amino group having 0-20 carbon atoms, an acyl         group, a carbonyl group, a carboxylic acid group, an ester         group, a cyano group, an isocyano group, thioalkyl, sulfinyl,         sulfonyl, phosphino, and combinations thereof,     -   wherein, at least one of R_(x1) and R_(x2) is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring;     -   X₁, X₂, X₃ or X₄ is connected to the metal through a         metal-carbon bond or a metal-nitrogen bond.

A second object of the present disclosure is to provide an electroluminescent device, which includes an anode, a cathode, and an organic layer disposed between the anode and the cathode, wherein the organic layer comprises the metal complex according to the first object of the present disclosure.

A third object of the present disclosure is to provide a compound formulation, which comprises the metal complex according to the first object of the present disclosure.

A fourth object of the present disclosure is to provide a compound that can be used for preparing the metal complex according to the first object of the present disclosure.

The novel metal complex having a cyano-substituted ligand disclosed by the present disclosure can be used as a light-emitting material in an electroluminescent device. When used in electroluminescent devices, these novel compounds can provide better device performance, e.g., narrower full width at half maximum, lower voltage values, and higher quantum efficiency, and the like.

The present invention discloses a series of novel cyano-substituted metal complexes which unexpectedly show many characteristics, such as high efficiency, low voltage, and no obvious blue-shifted or red-shifted luminescence. The most unexpected is that they have a very narrow peak width of emitted light. These advantages will greatly help to improve the level and color saturation of green light devices.

DESCRIPTION OF DRAWINGS

FIG. 1 is a schematic diagram of an organic light-emitting device that may contain a metal complex and a compound formulation disclosed herein.

FIG. 2 is a schematic diagram of another organic light-emitting device that may contain a metal complex and a compound formulation disclosed herein.

FIG. 3 is a diagram showing a ligand L_(a) represented by Formula 1 as disclosed herein.

DETAILED DESCRIPTION

OLEDs can be fabricated on various types of substrates such as glass, plastic, and metal foil. FIG. 1 schematically shows the organic light emitting device 100 without limitation. The figures are not necessarily drawn to scale. Some of the layers in the figures can also be omitted as needed. Device 100 may include a substrate 101, an anode 110, a hole injection layer 120, a hole transport layer 130, an electron blocking layer 140, an emissive layer 150, a hole blocking layer 160, an electron transport layer 170, an electron injection layer 180 and a cathode 190. Device 100 may be fabricated by depositing the layers described in order. The properties and functions of these various layers, as well as example materials, are described in more detail in U.S. Pat. No. 7,279,704 at cols. 6-10, the contents of which are incorporated by reference herein in its entirety.

More examples for each of these layers are available. For example, a flexible and transparent substrate-anode combination is disclosed in U.S. Pat. No. 5,844,363, which is incorporated by reference herein in its entirety. An example of a p-doped hole transport layer is m-MTDATA doped with F₄-TCNQ at a molar ratio of 50:1, as disclosed in U.S. Patent Application Publication No. 2003/0230980, which is incorporated by reference herein in its entirety. Examples of host materials are disclosed in U.S. Pat. No. 6,303,238 to Thompson et al., which is incorporated by reference herein in its entirety. An example of an n-doped electron transport layer is BPhen doped with Li at a molar ratio of 1:1, as disclosed in U.S. Patent Application Publication No. 2003/0230980, which is incorporated by reference herein in its entirety. U.S. Pat. Nos. 5,703,436 and 5,707,745, which are incorporated by reference herein in their entireties, disclose examples of cathodes including composite cathodes having a thin layer of metal such as Mg:Ag with an overlying transparent, electrically-conductive, sputter-deposited ITO layer. The theory and use of blocking layers is described in more detail in U.S. Pat. No. 6,097,147 and U.S. Patent Application Publication No. 2003/0230980, which are incorporated by reference herein in their entireties. Examples of injection layers are provided in U.S. Patent Application Publication No. 2004/0174116, which is incorporated by reference herein in its entirety. A description of protective layers may be found in U.S. Patent Application Publication No. 2004/0174116, which is incorporated by reference herein in its entirety.

The layered structure described above is provided by way of non-limiting example. Functional OLEDs may be achieved by combining the various layers described in different ways, or layers may be omitted entirely. It may also include other layers not specifically described. Within each layer, a single material or a mixture of multiple materials can be used to achieve optimum performance. Any functional layer may include several sublayers. For example, the emissive layer may have two layers of different emitting materials to achieve desired emission spectrum.

In one embodiment, an OLED may be described as having an “organic layer” disposed between a cathode and an anode. This organic layer may comprise a single layer or multiple layers.

An OLED can be encapsulated by a barrier layer. FIG. 2 schematically shows the organic light emitting device 200 without limitation. FIG. 2 differs from FIG. 1 in that the organic light emitting device include a barrier layer 102, which is above the cathode 190, to protect it from harmful species from the environment such as moisture and oxygen. Any material that can provide the barrier function can be used as the barrier layer such as glass and organic-inorganic hybrid layers. The barrier layer should be placed directly or indirectly outside of the OLED device. Multilayer thin film encapsulation was described in U.S. Pat. No. 7,968,146, which is herein incorporated by reference in its entirety.

Devices fabricated in accordance with embodiments of the present disclosure can be incorporated into a wide variety of consumer products that have one or more of the electronic component modules (or units) incorporated therein. Some examples of such consumer products include flat panel displays, monitors, medical monitors, televisions, billboards, lights for interior or exterior illumination and/or signaling, heads-up displays, fully or partially transparent displays, flexible displays, smart phones, tablets, phablets, wearable devices, smart watches, laptop computers, digital cameras, camcorders, viewfinders, micro-displays, 3-D displays, vehicles displays, and vehicle tail lights.

The materials and structures described herein may be used in other organic electronic devices listed above.

As used herein, “top” means furthest away from the substrate, while “bottom” means closest to the substrate. Where a first layer is described as “disposed over” a second layer, the first layer is disposed further away from substrate. There may be other layers between the first and second layer, unless it is specified that the first layer is “in contact with” the second layer. For example, a cathode may be described as “disposed over” an anode, even though there are various organic layers in between.

As used herein, “solution processible” means capable of being dissolved, dispersed, or transported in and/or deposited from a liquid medium, either in solution or suspension form.

A ligand may be referred to as “photoactive” when it is believed that the ligand directly contributes to the photoactive properties of an emissive material. A ligand may be referred to as “ancillary” when it is believed that the ligand does not contribute to the photoactive properties of an emissive material, although an ancillary ligand may alter the properties of a photoactive ligand.

It is believed that the internal quantum efficiency (IQE) of fluorescent OLEDs can exceed the 25% spin statistics limit through delayed fluorescence. As used herein, there are two types of delayed fluorescence, i.e. P-type delayed fluorescence and E-type delayed fluorescence. P-type delayed fluorescence is generated from triplet-triplet annihilation (TTA).

On the other hand, E-type delayed fluorescence does not rely on the collision of two triplets, but rather on the transition between the triplet states and the singlet excited states. Compounds that are capable of generating E-type delayed fluorescence are required to have very small singlet-triplet gaps to convert between energy states. Thermal energy can activate the transition from the triplet state back to the singlet state. This type of delayed fluorescence is also known as thermally activated delayed fluorescence (TADF). A distinctive feature of TADF is that the delayed component increases as temperature rises. If the reverse intersystem crossing rate is fast enough to minimize the non-radiative decay from the triplet state, the fraction of back populated singlet excited states can potentially reach 75%. The total singlet fraction can be 100%, far exceeding 25% of the spin statistics limit for electrically generated excitons.

E-type delayed fluorescence characteristics can be found in an exciplex system or in a single compound. Without being bound by theory, it is believed that E-type delayed fluorescence requires the luminescent material to have a small singlet-triplet energy gap (ΔE_(S-T)). Organic, non-metal containing, donor-acceptor luminescent materials may be able to achieve this. The emission in these materials is often characterized as a donor-acceptor charge-transfer (CT) type emission. The spatial separation of the HOMO and LUMO in these donor-acceptor type compounds often results in small ΔE_(S-T). These states may involve CT states. Often, donor-acceptor luminescent materials are constructed by connecting an electron donor moiety such as amino- or carbazole-derivatives and an electron acceptor moiety such as N-containing six-membered aromatic rings.

Definition of Terms of Substituents

Halogen or halide—as used herein includes fluorine, chlorine, bromine, and iodine.

Alkyl—contemplates both straight and branched chain alkyl groups. Examples of the alkyl group include methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, s-butyl group, isobutyl group, t-butyl group, n-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decyl group, n-undecyl group, n-dodecyl group, n-tridecyl group, n-tetradecyl group, n-pentadecyl group, n-hexadecyl group, n-heptadecyl group, n-octadecyl group, neopentyl group, 1-methylpentyl group, 2-methylpentyl group, 1-pentylhexyl group, 1-butylpentyl group, 1-heptyloctyl group, and 3-methylpentyl group. Additionally, the alkyl group may be optionally substituted. The carbons in the alkyl chain can be replaced by other hetero atoms. Of the above, preferred are methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, s-butyl group, isobutyl group, t-butyl group, n-pentyl group, and neopentyl group.

Cycloalkyl—as used herein contemplates cyclic alkyl groups. Preferred cycloalkyl groups are those containing 4 to 10 ring carbon atoms and includes cyclobutyl, cyclopentyl, cyclohexyl, 4-methylcyclohexyl, 4,4-dimethylcylcohexyl, 1-adamantyl, 2-adamantyl, 1-norbornyl, 2-norbornyl and the like. Additionally, the cycloalkyl group may be optionally substituted. The carbons in the ring can be replaced by other hetero atoms.

Alkenyl—as used herein contemplates both straight and branched chain alkene groups.

Preferred alkenyl groups are those containing 2 to 15 carbon atoms. Examples of the alkenyl group include vinyl group, allyl group, 1-butenyl group, 2-butenyl group, 3-butenyl group, 1,3-butandienyl group, 1-methylvinyl group, styryl group, 2,2-diphenylvinyl group, 1,2-diphenylvinyl group, 1-methylallyl group, 1,1-dimethylallyl group, 2-methylallyl group, 1-phenylallyl group, 2-phenylallyl group, 3-phenylallyl group, 3,3-diphenylallyl group, 1,2-dimethylallyl group, 1-phenyll-butenyl group, and 3-phenyl-1-butenyl group. Additionally, the alkenyl group may be optionally substituted.

Alkynyl—as used herein contemplates both straight and branched chain alkyne groups. Preferred alkynyl groups are those containing 2 to 15 carbon atoms. Additionally, the alkynyl group may be optionally substituted.

Aryl or aromatic group—as used herein includes noncondensed and condensed systems. Preferred aryl groups are those containing six to sixty carbon atoms, preferably six to twenty carbon atoms, more preferably six to twelve carbon atoms. Examples of the aryl group include phenyl, biphenyl, terphenyl, triphenylene, tetraphenylene, naphthalene, anthracene, phenalene, phenanthrene, fluorene, pyrene, chrysene, perylene, and azulene, preferably phenyl, biphenyl, terphenyl, triphenylene, fluorene, and naphthalene. Additionally, the aryl group may be optionally substituted. Examples of the non-condensed aryl group include phenyl group, biphenyl-2-yl group, biphenyl-3-yl group, biphenyl-4-yl group, p-terphenyl-4-yl group, p-terphenyl-3-yl group, p-terphenyl-2-yl group, m-terphenyl-4-yl group, m-terphenyl-3-yl group, m-terphenyl-2-yl group, o-tolyl group, m-tolyl group, p-tolyl group, p-t-butylphenyl group, p-(2-phenylpropyl)phenyl group, 4′-methylbiphenylyl group, 4″-t-butyl p-terphenyl-4-yl group, o-cumenyl group, m-cumenyl group, p-cumenyl group, 2,3-xylyl group, 3,4-xylyl group, 2,5-xylyl group, mesityl group, and m-quarterphenyl group.

Heterocyclic group or heterocycle—as used herein includes aromatic and non-aromatic cyclic groups. Hetero-aromatic also means heteroaryl. Preferred non-aromatic heterocyclic groups are those containing 3 to 7 ring atoms which include at least one hetero atom such as nitrogen, oxygen, and sulfur. The heterocyclic group can also be an aromatic heterocyclic group having at least one heteroatom selected from nitrogen atom, oxygen atom, sulfur atom, and selenium atom.

Heteroaryl—as used herein includes noncondensed and condensed hetero-aromatic groups that may include from one to five heteroatoms. Preferred heteroaryl groups are those containing three to thirty carbon atoms, preferably three to twenty carbon atoms, more preferably three to twelve carbon atoms. Suitable heteroaryl groups include dibenzothiophene, dibenzofuran, dibenzoselenophene, furan, thiophene, benzofuran, benzothiophene, benzoselenophene, carbazole, indolocarbazole, pyridylindole, pyrrolodipyridine, pyrazole, imidazole, triazole, oxazole, thiazole, oxadiazole, oxatriazole, dioxazole, thiadiazole, pyridine, pyridazine, pyrimidine, pyrazine, triazine, oxazine, oxathiazine, oxadiazine, indole, benzimidazole, indazole, indoxazine, benzoxazole, benzisoxazole, benzothiazole, quinoline, isoquinoline, cinnoline, quinazoline, quinoxaline, naphthyridine, phthalazine, pteridine, xanthene, acridine, phenazine, phenothiazine, phenoxazine, benzofuropyridine, furodipyridine, benzothienopyridine, thienodipyridine, benzoselenophenopyridine, and selenophenodipyridine, preferably dibenzothiophene, dibenzofuran, dibenzoselenophene, carbazole, indolocarbazole, imidazole, pyridine, triazine, benzimidazole, 1,2-azaborine, 1,3-azaborine, 1,4-azaborine, borazine, and aza-analogs thereof. Additionally, the heteroaryl group may be optionally substituted.

Alkoxy—it is represented by —O-Alkyl. Examples and preferred examples thereof are the same as those described above. Examples of the alkoxy group having 1 to 20 carbon atoms, preferably 1 to 6 carbon atoms include methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, and hexyloxy group. The alkoxy group having 3 or more carbon atoms may be linear, cyclic or branched.

Aryloxy—it is represented by —O-Aryl or —O-heteroaryl. Examples and preferred examples thereof are the same as those described above. Examples of the aryloxy group having 6 to 40 carbon atoms include phenoxy group and biphenyloxy group.

Arylalkyl—as used herein contemplates an alkyl group that has an aryl substituent. Additionally, the arylalkyl group may be optionally substituted. Examples of the arylalkyl group include benzyl group, 1-phenylethyl group, 2-phenylethyl group, 1-phenylisopropyl group, 2-phenylisopropyl group, phenyl-t-butyl group, alpha.-naphthylmethyl group, 1-alpha.-naphthylethyl group, 2-alpha-naphthylethyl group, 1-alpha-naphthylisopropyl group, 2-alpha-naphthylisopropyl group, beta-naphthylmethyl group, 1-beta-naphthylethyl group, 2-beta-naphthylethyl group, 1-beta-naphthylisopropyl group, 2-beta-naphthylisopropyl group, p-methylbenzyl group, m-methylbenzyl group, o-methylbenzyl group, p-chlorobenzyl group, m-chlorobenzyl group, o-chlorobenzyl group, p-bromobenzyl group, m-bromobenzyl group, o-bromobenzyl group, p-iodobenzyl group, m-iodobenzyl group, o-iodobenzyl group, p-hydroxybenzyl group, m-hydroxybenzyl group, o-hydroxybenzyl group, p-aminobenzyl group, m-aminobenzyl group, o-aminobenzyl group, p-nitrobenzyl group, m-nitrobenzyl group, o-nitrobenzyl group, p-cyanobenzyl group, m-cyanobenzyl group, o-cyanobenzyl group, 1-hydroxy-2-phenylisopropyl group, and 1-chloro-2-phenylisopropyl group. Of the above, preferred are benzyl group, p-cyanobenzyl group, m-cyanobenzyl group, o-cyanobenzyl group, 1-phenylethyl group, 2-phenylethyl group, 1-phenylisopropyl group, and 2-phenylisopropyl group.

The term “aza” in azadibenzofuran, aza-dibenzothiophene, etc. means that one or more of the C—H groups in the respective aromatic fragment are replaced by a nitrogen atom. For example, azatriphenylene encompasses dibenzo[f,h]quinoxaline, dibenzo[f,h]quinoline and other analogues with two or more nitrogens in the ring system. One of ordinary skill in the art can readily envision other nitrogen analogs of the aza-derivatives described above, and all such analogs are intended to be encompassed by the terms as set forth herein.

The alkyl, cycloalkyl, alkenyl, alkynyl, arylalkyl, heterocyclic group, aryl, and heteroaryl may be unsubstituted or may be substituted with one or more substituents selected from the group consisting of deuterium, halogen, alkyl, cycloalkyl, arylalkyl, alkoxy, aryloxy, amino, cyclic amino, silyl, alkenyl, cycloalkenyl, heteroalkenyl, alkynyl, aryl, heteroaryl, an acyl group, a carbonyl group, a carboxylic acid group, an ether group, an ester group, a nitrile group, an isonitrile group, a thioalkyl group, a sulfinyl group, a sulfonyl group, a phosphino group, and combinations thereof.

It is to be understood that when a molecular fragment is described as being a substituent or otherwise attached to another moiety, its name may be written as if it were a fragment (e.g. phenyl, phenylene, naphthyl, dibenzofuryl) or as if it were the whole molecule (e.g. benzene, naphthalene, dibenzofuran). As used herein, these different ways of designating a substituent or attached fragment are considered to be equivalent.

In the compounds mentioned in this disclosure, the hydrogen atoms can be partially or fully replaced by deuterium. Other atoms such as carbon and nitrogen, can also be replaced by their other stable isotopes. The replacement by other stable isotopes in the compounds may be preferred due to its enhancements of device efficiency and stability.

In the compounds mentioned in this disclosure, multiple substitutions refer to a range that includes a double substitution, up to the maximum available substitutions. When a substitution in the compounds mentioned in this disclosure represents multiple substitutions (including di, tri, tetra substitutions etc.), that means the substituent may exist at a plurality of available substitution positions on its linking structure, the substituents present at a plurality of available substitution positions may be the same structure or different structures.

In the compounds mentioned in this disclosure, the expression that adjacent substituents can be optionally joined to form a ring is intended to be taken to mean that two radicals are linked to each other by a chemical bond. This is illustrated by the following scheme:

Furthermore, the expression that adjacent substituents can be optionally joined to form a ring is also intended to be taken to mean that in the case where one of the two radicals represents hydrogen, the second radical is bonded at a position to which the hydrogen atom was bonded, with formation of a ring. This is illustrated by the following scheme:

According to an embodiment of the present disclosure, a metal complex having a L_(a) ligand is disclosed, wherein L_(a) comprises a structure represented by Formula 1:

-   -   wherein, Cy is a substituted or unsubstituted aryl or heteroaryl         group having 5 to 24 ring atoms;     -   wherein, Cy is bonded to a metal through a metal-carbon bond or         a metal-nitrogen bond;     -   wherein, X₁ to X₄ are each independently selected from C,         CR_(x1) or N, and at least one of X₁ to X₄ is C and connected to         Cy; when more than one of X₁ to X₄ is CR_(x1), the R_(x1) may be         the same or different;     -   wherein, X₅ to X₈ are each independently selected from CR_(x2)         or N; when more than one of X₅ to X₈ is CR_(x2), the R_(x2) may         be the same or different;     -   X is selected from the group consisting of O, S, Se, NR_(x3),         CR_(x4)R_(x5) and SiR_(x6)R_(x7); wherein, R_(x1), R_(x2),         R_(x3), R_(x4), R_(x5), R_(x6) and R_(x7) are each independently         selected from the group consisting of hydrogen, deuterium,         halogen, a substituted or unsubstituted alkyl group having 1-20         carbon atoms, a substituted or unsubstituted cycloalkyl group         having 3-20 ring carbon atoms, a substituted or unsubstituted         heteroalkyl group having 1-20 carbon atoms, a substituted or         unsubstituted arylalkyl group having 7-30 carbon atoms, a         substituted or unsubstituted alkoxy group having 1-20 carbon         atoms, a substituted or unsubstituted aryloxy group having 6-30         carbon atoms, a substituted or unsubstituted alkenyl group         having 2-20 carbon atoms, a substituted or unsubstituted aryl         group having 6-30 carbon atoms, a substituted or unsubstituted         heteroaryl group having 3-30 carbon atoms, a substituted or         unsubstituted alkylsilyl group having 3-20 carbon atoms, a         substituted or unsubstituted arylsilyl group having 6-20 carbon         atoms, a substituted or unsubstituted amino group having 0-20         carbon atoms, an acyl group, a carbonyl group, a carboxylic acid         group, an ester group, a cyano group, an isocyano group,         thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations         thereof,     -   wherein, at least one of R_(x1) and R_(x2) is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring;     -   X₁, X₂, X₃ or X₄ is connected to the metal through a         metal-carbon bond or a metal-nitrogen bond.

According to an embodiment of the present disclosure, Cy is any structure selected from the group consisting of:

-   -   wherein     -   R may represent mono-substitution, up to the maximum available         multi-substitution, or no substitution; when more than one R         exists in any of the above structures, the R may be the same or         different;     -   wherein, R is independently selected from the group consisting         of hydrogen, deuterium, halogen, a substituted or unsubstituted         alkyl group having 1-20 carbon atoms, a substituted or         unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a         substituted or unsubstituted heteroalkyl group having 1-20         carbon atoms, a substituted or unsubstituted arylalkyl group         having 7-30 carbon atoms, a substituted or unsubstituted alkoxy         group having 1-20 carbon atoms, a substituted or unsubstituted         aryloxy group having 6-30 carbon atoms, a substituted or         unsubstituted alkenyl group having 2-20 carbon atoms, a         substituted or unsubstituted aryl group having 6-30 carbon         atoms, a substituted or unsubstituted heteroaryl group having         3-30 carbon atoms, a substituted or unsubstituted alkylsilyl         group having 3-20 carbon atoms, a substituted or unsubstituted         arylsilyl group having 6-20 carbon atoms, a substituted or         unsubstituted amino group having 0-20 carbon atoms, an acyl         group, a carbonyl group, a carboxylic acid group, an ester         group, a cyano group, an isocyano group, thioalkyl, sulfinyl,         sulfonyl, phosphino, and combinations thereof;     -   any two adjacent substituents can optionally be joined to form a         ring;     -   wherein, “#” represents a position at which the metal is         connected, and “*” represents a position at which X₁, X₂, X₃ or         X₄ is connected.

According to an embodiment of the present disclosure, the metal complex has a general formula of M(L_(a))_(m)(L_(b))_(n)(L_(c))_(q), wherein L_(a) is a first ligand coordinated to the metal M, and L_(b) and L_(c) are a second ligand and a third ligand coordinated to the metal M, respectively, wherein L_(b) and L_(c) may be the same or different; L_(a), L_(b) and L_(c) can optionally be linked to form a multidentate ligand;

-   -   wherein, m is 1, 2 or 3, n is 0, 1 or 2, q is 0, 1 or 2, and         m+n+q is equal to the oxidation state of M;     -   wherein, the metal M is selected from the group consisting of         Cu, Ag, Au, Ru, Rh, Pd, Os, Ir, and Pt; preferably, wherein, the         metal M is selected from Pt, Os or Ir;     -   wherein, L_(a) is independently selected from the group         consisting of:

-   -   wherein, in the structure of L_(a),     -   X is selected from the group consisting of O, S, Se, NR_(x3),         CR_(x4)R_(x5) and SiR_(x6)R_(x7);     -   R₁, R₂, R₃ and R₄ may represent mono-, di-, tri- or         tetra-substitution, or no substitution; R₁, R₂, R₃, R₄, R_(x3),         R_(x4), R_(x5), R_(x6) and R_(x7) are each independently         selected from the group consisting of hydrogen, deuterium,         halogen, a substituted or unsubstituted alkyl group having 1-20         carbon atoms, a substituted or unsubstituted cycloalkyl group         having 3-20 ring carbon atoms, a substituted or unsubstituted         heteroalkyl group having 1-20 carbon atoms, a substituted or         unsubstituted arylalkyl group having 7-30 carbon atoms, a         substituted or unsubstituted alkoxy group having 1-20 carbon         atoms, a substituted or unsubstituted aryloxy group having 6-30         carbon atoms, a substituted or unsubstituted alkenyl group         having 2-20 carbon atoms, a substituted or unsubstituted aryl         group having 6-30 carbon atoms, a substituted or unsubstituted         heteroaryl group having 3-30 carbon atoms, a substituted or         unsubstituted alkylsilyl group having 3-20 carbon atoms, a         substituted or unsubstituted arylsilyl group having 6-20 carbon         atoms, a substituted or unsubstituted amino group having 0-20         carbon atoms, an acyl group, a carbonyl group, a carboxylic acid         group, an ester group, a cyano group, an isocyano group,         thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations         thereof,     -   wherein, at least one of R₃ and R₄ is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring;     -   wherein, L_(b) and L_(c) are independently selected from the         group consisting of:

-   -   wherein     -   R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or         tetra-substitution, or no substitution;     -   X_(b) is selected from the group consisting of: O, S, Se,         NR_(N1), and CR_(C1)R_(C2);     -   R_(a), R_(b), R_(c), R_(N1), R_(C1) and R_(C2) are each         independently selected from the group consisting of hydrogen,         deuterium, halogen, a substituted or unsubstituted alkyl group         having 1-20 carbon atoms, a substituted or unsubstituted         cycloalkyl group having 3-20 ring carbon atoms, a substituted or         unsubstituted heteroalkyl group having 1-20 carbon atoms, a         substituted or unsubstituted arylalkyl group having 7-30 carbon         atoms, a substituted or unsubstituted alkoxy group having 1-20         carbon atoms, a substituted or unsubstituted aryloxy group         having 6-30 carbon atoms, a substituted or unsubstituted alkenyl         group having 2-20 carbon atoms, a substituted or unsubstituted         aryl group having 6-30 carbon atoms, a substituted or         unsubstituted heteroaryl group having 3-30 carbon atoms, a         substituted or unsubstituted alkylsilyl group having 3-20 carbon         atoms, a substituted or unsubstituted arylsilyl group having         6-20 carbon atoms, a substituted or unsubstituted amino group         having 0-20 carbon atoms, an acyl group, a carbonyl group, a         carboxylic acid group, an ester group, a cyano group, an         isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and         combinations thereof;     -   any two adjacent substituents can optionally be joined to form a         ring.

According to an embodiment of the present disclosure, in the structural formula of the ligand L_(a), X is selected from O, S or Se.

According to an embodiment of the present disclosure, the metal complex has any one of the structures according to Formula 2 to Formula 10:

-   -   wherein     -   m is 1, 2 or 3;     -   X is selected from 0, S or Se;     -   R₁, R₃, and R₄ may represent mono-, di-, tri- or         tetra-substitution, or no substitution;     -   R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or         tetra-substitution, or no substitution;     -   R₁, R₃, R₄, R_(a), R_(b) and R_(c) are each independently         selected from the group consisting of hydrogen, deuterium,         halogen, a substituted or unsubstituted alkyl group having 1-20         carbon atoms, a substituted or unsubstituted cycloalkyl group         having 3-20 ring carbon atoms, a substituted or unsubstituted         heteroalkyl group having 1-20 carbon atoms, a substituted or         unsubstituted arylalkyl group having 7-30 carbon atoms, a         substituted or unsubstituted alkoxy group having 1-20 carbon         atoms, a substituted or unsubstituted aryloxy group having 6-30         carbon atoms, a substituted or unsubstituted alkenyl group         having 2-20 carbon atoms, a substituted or unsubstituted aryl         group having 6-30 carbon atoms, a substituted or unsubstituted         heteroaryl group having 3-30 carbon atoms, a substituted or         unsubstituted alkylsilyl group having 3-20 carbon atoms, a         substituted or unsubstituted arylsilyl group having 6-20 carbon         atoms, a substituted or unsubstituted amino group having 0-20         carbon atoms, an acyl group, a carbonyl group, a carboxylic acid         group, an ester group, a cyano group, an isocyano group,         thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations         thereof;     -   wherein, at least one of R₃ and R₄ is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring.

According to an embodiment of the present disclosure, the metal complex has the structure of Formula 2-a:

-   -   wherein,     -   m is 1, 2 or 3;     -   X is selected from 0, S or Se;     -   R₃ and R₄ may represent mono-, di-, tri- or tetra-substitution,         or no substitution;     -   R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or         tetra-substitution, or no substitution;     -   wherein, R₁₁, R₁₂, R₁₃, R₁₄, R₃, R₄, R_(a), and R_(b) are each         independently selected from the group consisting of hydrogen,         deuterium, halogen, a substituted or unsubstituted alkyl group         having 1-20 carbon atoms, a substituted or unsubstituted         cycloalkyl group having 3-20 ring carbon atoms, a substituted or         unsubstituted heteroalkyl group having 1-20 carbon atoms, a         substituted or unsubstituted arylalkyl group having 7-30 carbon         atoms, a substituted or unsubstituted alkoxy group having 1-20         carbon atoms, a substituted or unsubstituted aryloxy group         having 6-30 carbon atoms, a substituted or unsubstituted alkenyl         group having 2-20 carbon atoms, a substituted or unsubstituted         aryl group having 6-30 carbon atoms, a substituted or         unsubstituted heteroaryl group having 3-30 carbon atoms, a         substituted or unsubstituted alkylsilyl group having 3-20 carbon         atoms, a substituted or unsubstituted arylsilyl group having         6-20 carbon atoms, a substituted or unsubstituted amino group         having 0-20 carbon atoms, an acyl group, a carbonyl group, a         carboxylic acid group, an ester group, a cyano group, an         isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and         combinations thereof,     -   wherein, at least one of R₃ and R₄ is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring.

According to an embodiment of the present disclosure, when at least one of R₁₁ and R₁₄ in Formula 2-a is not hydrogen, R₁₂ and R₁₃ are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.

According to an embodiment of the present disclosure, when R₁ and R₁₄ in Formula 2-a are both hydrogen, R₁₂ and R₁₃ are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, and the total number of carbon atoms in R₁₂ and R₁₃ is less than or equal to 1.

According to an embodiment of the present disclosure, at least one of X₅ to X₈ in the Formula 1 is CR_(x2), and the R_(x2) is a cyano group.

According to an embodiment of the present disclosure, X₅ to X₈ in the Formula 1 are each independently selected from CR_(x2), and at least one of the R_(x2) is a cyano group.

According to an embodiment of the present disclosure, R₄ may represent mono-, di-, tri- or tetra-substitution; when more than one R₄ exists, the R₄ may be the same or different; R₄ is selected from the group consisting of deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a cyano group, and combinations thereof; and at least one R₄ is a cyano group.

According to an embodiment of the present disclosure, the ligand L_(a) is selected from the group consisting of L_(a1) to L_(a575). The specific structures of L_(a1) to L_(a575) are described in claim 8.

According to an embodiment of the present disclosure, the ligand L_(a) is selected from the group consisting of L_(a1) to L_(a957). The specific structures of L_(a1) to L_(a957) are described in claim 8.

According to an embodiment of the present disclosure, the hydrogen in L_(a) can be partially or fully deuterated.

According to an embodiment of the present disclosure, the hydrogen on the aryl group in L_(a) can be partially or fully deuterated.

According to an embodiment of the present disclosure, the hydrogen on the alkyl group in L_(a) can be partially or fully deuterated.

According to an embodiment of the present disclosure, the hydrogen in L_(a) can be partially or fully deuterated, and the ligand L_(a) is selected from the group consisting of L_(a958) to L_(a1019), wherein the specific structures of L_(a958) to L_(a1019) are described in claim 14.

According to an embodiment of the present disclosure, the metal complex has the Formula IrL_(a)(L_(b))₂ or Ir(L_(a))₂L_(b), wherein L_(a) is one or two selected from L_(a1) to L_(a575), and L_(b) is one or two selected from the group consisting of L_(b1)-L_(b41), wherein the specific structures of L_(b1)-L_(b41) are described in claim 17.

According to an embodiment of the present disclosure, the metal complex has the Formula IrL_(a)(L_(b))₂ or Ir(L_(a))₂L_(b), wherein L_(a) is one or two selected from L_(a1) to L_(a1019), and L_(b) is one or two selected from the group consisting of:

According to an embodiment of the present disclosure, the metal complex has the Formula Ir(L_(a))₂L_(c) or IrL_(a)(L_(c))₂, wherein L_(a) is one or two selected from L_(a1) to L_(a1019), and L_(c) is one or two selected from the group consisting of L_(c1) to L_(c360), wherein the specific structures of L_(c1) to L_(c360) are described in claim 18.

According to an embodiment of the present disclosure, the metal complex has a structure represented by any one selected from Metal complex 1 to Metal complex 316:

Wherein Metal complex 1 to Metal complex 226 have the structure of IrL_(a)(L_(b))₂, wherein the two L_(b) are the same, wherein L_(a) and L_(b) correspond to the structures as shown in the following table, respectively:

Metal Metal complex L_(a) L_(b) complex L_(a) L_(b) 1 L_(a1) L_(b1) 2 L_(a2) L_(b1) 3 L_(a3) L_(b1) 4 L_(a4) L_(b1) 5 L_(a121) L_(b1) 6 L_(a122) L_(b1) 7 L_(a123) L_(b1) 8 L_(a137) L_(b1) 9 L_(a138) L_(b1) 10 L_(a139) L_(b1) 11 L_(a153) L_(b1) 12 L_(a154) L_(b1) 13 L_(a155) L_(b1) 14 L_(a169) L_(b1) 15 L_(a170) L_(b1) 16 L_(a171) L_(b1) 17 L_(a221) L_(b1) 18 L_(a222) L_(b1) 19 L_(a293) L_(b1) 20 L_(a294) L_(b1) 21 L_(a295) L_(b1) 22 L_(a297) L_(b1) 23 L_(a298) L_(b1) 24 L_(a299) L_(b1) 25 L_(a313) L_(b1) 26 L_(a314) L_(b1) 27 L_(a415) L_(b1) 28 L_(a416) L_(b1) 29 L_(a467) L_(b1) 30 L_(a468) L_(b1) 31 L_(a487) L_(b1) 32 L_(a488) L_(b1) 33 L_(a507) L_(b1) 34 L_(a508) L_(b1) 35 L_(a516) L_(b1) 36 L_(a517) L_(b1) 37 L_(a527) L_(b1) 38 L_(a528) L_(b1) 39 L_(a547) L_(b1) 40 L_(a548) L_(b1) 41 L_(a576) L_(b1) 42 L_(a577) L_(b1) 43 L_(a592) L_(b1) 44 L_(a593) L_(b1) 45 L_(a640) L_(b1) 46 L_(a652) L_(b1) 47 L_(a692) L_(b1) 48 L_(a693) L_(b1) 49 L_(a704) L_(b1) 50 L_(a842) L_(b1) 51 L_(a854) L_(b) 52 L_(a896) L_(b1) 53 L_(a962) L_(b) 54 L_(a966) L_(b1) 55 L_(a970) L_(b) 56 L_(a973) L_(b1) 57 L_(a974) L_(b1) 58 L_(a975) L_(b1) 59 L_(a976) L_(b1) 60 L_(a978) L_(b1) 61 L_(a985) L_(b1) 62 L_(a987) L_(b1) 63 L_(a988) L_(b) 64 L_(a999) L_(b1) 65 L_(a1003) L_(b1) 66 L_(a1010) L_(b1) 67 L_(al) L_(b3) 68 L_(a2) L_(b3) 69 L_(a3) L_(b3) 70 L_(a4) L_(b3) 71 L_(a121) L_(b3) 72 L_(a122) L_(b3) 73 L_(a123) L_(b3) 74 L_(a137) L_(b3) 75 L_(a138) L_(b3) 76 L_(a139) L_(b3) 77 L_(a293) L_(b3) 78 L_(a294) L_(b3) 79 L_(a297) L_(b3) 80 L_(a298) L_(b3) 81 L_(a576) L_(b3) 82 L_(a577) L_(b3) 83 L_(a592) L_(b3) 84 L_(a593) L_(b3) 85 L_(a640) L_(b3) 86 L_(a652) L_(b3) 87 L_(a692) L_(b3) 88 L_(a693) L_(b3) 89 L_(a704) L_(b3) 90 L_(a842) L_(b3) 91 L_(a854) L_(b3) 92 L_(a896) L_(b3) 93 L_(a962) L_(b3) 94 L_(a966) L_(b3) 95 L_(a970) L_(b3) 96 L_(a973) L_(b3) 97 L_(a974) L_(b3) 98 L_(a975) L_(b3) 99 L_(a976) L_(b3) 100 L_(a978) L_(b3) 101 L_(a985) L_(b3) 102 L_(a987) L_(b3) 103 L_(a988) L_(b3) 104 L_(a999) L_(b3) 105 L_(a1003) L_(b3) 106 L_(a1010) L_(b3) 107 L_(al) L_(b4) 108 L_(a2) L_(b4) 109 L_(a3) L_(b4) 110 L_(a4) L_(b4) 111 L_(a121) L_(b4) 112 L_(a122) L_(b4) 113 L_(a123) L_(b4) 114 L_(a137) L_(b4) 115 L_(a138) L_(b4) 116 L_(a139) L_(b4) 117 L_(a293) L_(b4) 118 L_(a294) L_(b4) 119 L_(a297) L_(b4) 120 L_(a298) L_(b4) 121 L_(a576) L_(b4) 122 L_(a577) L_(b4) 123 L_(a592) L_(b4) 124 L_(a593) L_(b4) 125 L_(a640) L_(b4) 126 L_(a652) L_(b4) 127 L_(a692) L_(b4) 128 L_(a693) L_(b4) 129 L_(a704) L_(b4) 130 L_(a842) L_(b4) 131 L_(a854) L_(b4) 132 L_(a896) L_(b4) 133 L_(a962) L_(b4) 134 L_(a966) L_(b4) 135 L_(a970) L_(b4) 136 L_(a973) L_(b4) 137 L_(a974) L_(b4) 138 L_(a975) L_(b4) 139 L_(a976) L_(b4) 140 L_(a978) L_(b4) 141 L_(a985) L_(b4) 142 L_(a987) L_(b4) 143 L_(a988) L_(b4) 144 L_(a999) L_(b4) 145 L_(a1003) L_(b4) 146 L_(a1010) L_(b4) 147 L_(a1) L_(b8) 148 L_(a2) L_(b8) 149 L_(a3) L_(b8) 150 L_(a4) L_(b8) 151 L_(a121) L_(b8) 152 L_(a122) L_(b8) 153 L_(a123) L_(b8) 154 L_(a137) L_(b8) 155 L_(a138) L_(b8) 156 L_(a139) L_(b8) 157 L_(a293) L_(b8) 158 L_(a294) L_(b8) 159 L_(a297) L_(b8) 160 L_(a298) L_(b8) 161 L_(a576) L_(b8) 162 L_(a577) L_(b8) 163 L_(a592) L_(b8) 16 L_(a593) L_(b8) 165 L_(a640) L_(b8) 166 L_(a652) L_(b8) 167 L_(a692) L_(b8) 168 L_(a693) L_(b8) 169 L_(a704) L_(b8) 170 L_(a842) L_(b8) 171 L_(a854) L_(b8) 172 L_(a896) L_(b8) 173 L_(a962) L_(b8) 174 L_(a966) L_(b8) 175 L_(a970) L_(b8) 176 L_(a973) L_(b8) 177 L_(a974) L_(b8) 178 L_(a975) L_(b8) 179 L_(a976) L_(b8) 180 L_(a978) L_(b8) 181 L_(a985) L_(b8) 182 L_(a987) L_(b8) 183 L_(a988) L_(b8) 184 L_(a999) L_(b8) 185 L_(a1003) L_(b8) 186 L_(a1010) L_(b8) 187 L_(a1) L_(b30) 188 L_(a2) L_(b30) 189 L_(a3) L_(b30) 190 L_(a4) L_(b30) 191 L_(a121) L_(b30) 192 L_(a122) L_(b30) 193 L_(a123) L_(b30) 194 L_(a137) L_(b30) 195 L_(a138) L_(b30) 196 L_(a139) L_(b30) 197 L_(a293) L_(b30) 198 L_(a294) L_(b30) 199 L_(a297) L_(b30) 200 L_(a298) L_(b30) 201 L_(a576) L_(b30) 202 L_(a577) L_(b30) 203 L_(a592) L_(b30) 204 L_(a593) L_(b30) 205 L_(a640) L_(b30) 206 L_(a652) L_(b30) 207 L_(a692) L_(b30) 208 L_(a693) L_(b30) 209 L_(a704) L_(b30) 210 L_(a842) L_(b30) 211 L_(a854) L_(b30) 212 L_(a896) L_(b30) 213 L_(a962) L_(b30) 214 L_(a966) L_(b30) 215 L_(a970) L_(b30) 216 L_(a973) L_(b30) 217 L_(a974) L_(b30) 218 L_(a975) L_(b30) 219 L_(a976) L_(b30) 220 L_(a978) L_(b30) 221 L_(a985) L_(b30) 222 L_(a987) L_(b30) 223 L_(a988) L_(b30) 224 L_(a999) L_(b30) 225 L_(a1003) L_(b30) 226 L_(a1010) L_(b30)

Wherein Metal complex 227 to Metal complex 274 have the structure of Ir(L_(a))₂L_(c), wherein the two L_(a) are the same, wherein L_(a) and L_(c) correspond to the structures as shown in the following table, respectively:

Metal Metal complex L_(a) L_(c) complex L_(a) L_(c) 227 L_(a323) L_(c1) 228 L_(a324) L_(c1) 229 L_(a328) L_(c1) 230 L_(a329) L_(c1) 231 L_(a333) L_(c1) 232 L_(a334) L_(c1) 233 L_(a338) L_(c1) 234 L_(a339) L_(c1) 235 L_(a343) L_(c1) 236 L_(a344) L_(c1) 237 L_(a348) L_(c1) 238 L_(a349) L_(c1) 239 L_(a353) L_(c1) 240 L_(a354) L_(c1) 241 L_(a358) L_(c1) 242 L_(a359) L_(c1) 243 L_(a363) L_(c1) 244 L_(a364) L_(c1) 245 L_(a368) L_(c1) 246 L_(a369) L_(c1) 247 L_(a373) L_(c1) 248 L_(a374) L_(c1) 249 L_(a388) L_(c1) 250 L_(a389) L_(c1) 251 L_(a323) L₃₁ 252 L_(a324) L₃₁ 253 L_(a328) L₃₁ 254 L_(a329) L₃₁ 255 L_(a333) L₃₁ 256 L_(a334) L₃₁ 257 L_(a338) L₃₁ 258 L_(a339) L₃₁ 259 L_(a343) L₃₁ 260 L_(a344) L₃₁ 261 L_(a348) L₃₁ 262 L_(a349) L₃₁ 263 L_(a353) L₃₁ 264 L_(a354) L₃₁ 265 L_(a358) L₃₁ 266 L_(a359) L₃₁ 267 L_(a363) L₃₁ 268 L_(a364) L₃₁ 269 L_(a368) L₃₁ 270 L_(a369) L₃₁ 271 L_(a373) L₃₁ 272 L_(a374) L₃₁ 273 L_(a388) L₃₁ 274 L_(a389) L₃₁

Wherein Metal complex 275 to Metal complex 316 have the structure of Ir(L_(a))₃, wherein the three L_(a) are the same, wherein L_(a) corresponds to the structures as shown in the following table:

Metal complex L_(a) 275 L_(a1) 276 L_(a2) 277 L_(a3) 278 L_(a121) 279 L_(a122) 280 L_(a137) 281 L_(a138) 282 L_(a293) 283 L_(a297) 284 L_(a298) 285 L_(a487) 286 L_(a488) 287 L_(a507) 288 L_(a508) 289 L_(a547) 290 L_(a548) 291 L_(a576) 292 L_(a577) 293 L_(a640) 294 L_(a641) 295 L_(a652) 296 L_(a653) 297 L_(a692) 298 L_(a693) 299 L_(a704) 300 L_(a842) 301 L_(a854) 302 L_(a896) 303 L_(a962) 304 L_(a966) 305 L_(a970) 306 L_(a973) 307 L_(a974) 308 L_(a975) 309 L_(a976) 310 L_(a978) 311 L_(a985) 312 L_(a987) 313 L_(a988) 314 L_(a999) 315 L_(a1003) 316 L_(a1010)

According to an embodiment of the present disclosure, a compound selected from the group consisting of Compound 1 to Compound 136 is also disclosed. Wherein, the specific structures of Compound 1 to Compound 136 are described in claim 14.

According to an embodiment of the present disclosure, an electroluminescent device is also disclosed, which includes:

-   -   an anode,     -   a cathode, and     -   an organic layer disposed between the anode and the cathode,         wherein the organic layer comprises a metal complex comprising         the ligand L_(a) represented by Formula 1:

-   -   wherein, Cy is a substituted or unsubstituted aryl or heteroaryl         group having 5 to 24 ring atoms;     -   the Cy is bonded to a metal through a metal-carbon bond or a         metal-nitrogen bond;     -   X₁ to X₄ are each independently selected from C, CR_(x1) or N,         and at least one of X₁ to X₄ is C which is connected to the Cy;         when more than one of X₁ to X₄ is CR_(x1), the R_(x1) may be the         same or different;     -   X₅ to X₈ are each independently selected from CR_(x2) or N; when         more than one of X₅ to X₈ is CR_(x2), the R_(x2) may be the same         or different;     -   X is selected from the group consisting of O, S, Se, NR_(x3),         CR_(x4)R_(x5) and SiR_(x6)R_(x7);     -   R_(x1), R_(x2), R_(x3), R_(x4), R_(x5), R_(x6) and R_(x7) are         each independently selected from the group consisting of         hydrogen, deuterium, halogen, a substituted or unsubstituted         alkyl group having 1-20 carbon atoms, a substituted or         unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a         substituted or unsubstituted heteroalkyl group having 1-20         carbon atoms, a substituted or unsubstituted arylalkyl group         having 7-30 carbon atoms, a substituted or unsubstituted alkoxy         group having 1-20 carbon atoms, a substituted or unsubstituted         aryloxy group having 6-30 carbon atoms, a substituted or         unsubstituted alkenyl group having 2-20 carbon atoms, a         substituted or unsubstituted aryl group having 6-30 carbon         atoms, a substituted or unsubstituted heteroaryl group having         3-30 carbon atoms, a substituted or unsubstituted alkylsilyl         group having 3-20 carbon atoms, a substituted or unsubstituted         arylsilyl group having 6-20 carbon atoms, a substituted or         unsubstituted amino group having 0-20 carbon atoms, an acyl         group, a carbonyl group, a carboxylic acid group, an ester         group, a cyano group, an isocyano group, thioalkyl, sulfinyl,         sulfonyl, phosphino, and combinations thereof,     -   wherein, at least one of R_(x1) and R_(x2) is a cyano group;     -   any two adjacent substituents can optionally be joined to form a         ring;     -   X₁, X₂, X₃ or X₄ are connected to the metal through a         metal-carbon bond or a metal-nitrogen bond.

According to an embodiment of the present disclosure, in the electroluminescent device, the organic layer is a light-emitting layer, and the metal complex is a light-emitting material.

According to an embodiment of the present disclosure, in the electroluminescent device, the organic layer further includes a host material.

According to an embodiment of the present disclosure, in the electroluminescent device, the organic layer further includes at least two host materials.

According to an embodiment of the present disclosure, the host material comprises at least one chemical group selected from the group consisting of benzene, biphenyl, pyridine, pyrimidine, triazine, carbazole, azacarbazole, indolocarbazole, dibenzothiophene, azadibenzothiophen, dibenzofuran, azadibenzofuran, dibenzoselenophene, azadibenzoselenophene, triphenylene, azatriphenylene, fluorene, silicon-fluorene, naphthalene, quinoline, isoquinoline, quinazoline, quinoxaline, phenanthrene, azaphenanthrene, and combinations thereof.

According to an embodiment of the present disclosure, the electroluminescent device is incorporated into a device selected from the group consisting of a consumption product, an electronic component module, an organic light-emitting device and a lighting panel.

According to another embodiment of the present disclosure, a compound formulation is also disclosed, which comprises a metal complex. The specific structure of the metal complex is shown in any one of the foregoing embodiments.

Combination with Other Materials

The materials described in the present disclosure for a particular layer in an organic light emitting device can be used in combination with various other materials present in the device. The combinations of these materials are described in more detail in U.S. Pat. App. No. 20160359122 at paragraphs 0132-0161, which is incorporated by reference herein in its entirety. The materials described or referred to the disclosure are non-limiting examples of materials that may be useful in combination with the compounds disclosed herein, and one of skill in the art can readily consult the literature to identify other materials that may be useful in combination.

The materials described herein as useful for a particular layer in an organic light emitting device may be used in combination with a variety of other materials present in the device. For example, dopants disclosed herein may be used in combination with a wide variety of hosts, transport layers, blocking layers, injection layers, electrodes and other layers that may be present. The combination of these materials is described in detail in paragraphs 0080-0101 of U.S. Pat. App. No. 20150349273, which is incorporated by reference herein in its entirety. The materials described or referred to the disclosure are non-limiting examples of materials that may be useful in combination with the compounds disclosed herein, and one of skill in the art can readily consult the literature to identify other materials that may be useful in combination.

In the embodiments of material synthesis, all reactions were performed under nitrogen protection unless otherwise stated. All reaction solvents were anhydrous and used as received from commercial sources. Synthetic products were structurally confirmed and tested for properties using one or more conventional equipment in the art (including, but not limited to, nuclear magnetic resonance instrument produced by BRUKER, liquid chromatograph produced by SHIMADZU, liquid chromatograph-mass spectrometry produced by SHIMADZU, gas chromatograph-mass spectrometry produced by SHIMADZU, differential Scanning calorimeters produced by SHIMADZU, fluorescence spectrophotometer produced by SHANGHAI LENGGUANG TECH., electrochemical workstation produced by WUHAN CORRTEST, and sublimation apparatus produced by ANHUI BEQ, etc.) by methods well known to the persons skilled in the art. In the embodiments of the device, the characteristics of the device were also tested using conventional equipment in the art (including, but not limited to, evaporator produced by ANGSTROM ENGINEERING, optical testing system produced by SUZHOU FATAR, life testing system produced by SUZHOU FATAR, and ellipsometer produced by BEIJING ELLITOP, etc.) by methods well known to the persons skilled in the art. As the persons skilled in the art are aware of the above-mentioned equipment use, test methods and other related contents, the inherent data of the sample can be obtained with certainty and without influence, so the above related contents are not further described in this patent.

Synthesis Examples of the Materials:

The method for preparing the compound of the present disclosure is not limited, and the following compounds are exemplified as typical but non-limiting examples. The synthetic route and preparation method of which are as follows:

Synthesis Example 1: Synthesis of Compound IrL_(a1)(L_(b1))₂ (Metal Complex 1)

Step 1:

To a dried 1000 mL round bottom flask, 3-chloro-2-methoxyphenylboronic acid (20.00 g, 107.29 mmol), 2-fluoro-3-bromobenzonitrile (20.43 g, 102.20 mmol), tetrakis(triphenylphosphine)palladium (Pd(PPh₃)₄) (4.39 g, 3.74 mmol), potassium carbonate (32.48 g, 235.40 mmol), 1,4-dioxane (500 mL) and water (100 mL) were sequentially added. The reaction system was then replaced with N₂ three times and protected by N₂, then it was heated in a heating mantle and stirred under reflux for 12 h. After the reaction was cooled, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography, eluting with 5% (v/v) ethyl acetate (EA)/petroleum ether (PE), to give 22 g of white product intermediate 1 (74.8% yield).

Step 2:

In a dried 500 mL three-necked flask, intermediate 1 (22.00 g, 84.30 mmol) and dichloromethane (350 mL) were added. The reaction system was then replaced with N₂ three times and protected by N₂, and then stirred in an ice bath at 0° C. for 5 minutes. Boron tribromide was added dropwise thereto. After the completion of the addition, the reaction was warmed up to room temperature and stirred for 12 h. After the reaction was completed, the reaction was quenched with ice-water in an ice bath and neutralized with a saturated aqueous solution of sodium bicarbonate. A large amount of white solid product was precipitated, which was directly filtered, washed with water three times, and dried under reduced pressure to obtain 19.7 g of white solid product intermediate 2 (94.4% yield).

Step 3:

In a dried 500 mL round-bottomed flask, intermediate 2 (19.7 g, 79.6 mmol), potassium carbonate (32.9 g, 238.8 mmol) and DMF (300 mL) were added successively, and then the reaction was heated in a heating mantle at 100° C. and stirred for 12 h. After the reaction was completed, it was cooled and filtered through celite. The organic phase was washed with saturated brine, extracted twice with ethyl acetate, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography, eluting with a 20% (v/v) dichloromethane/petroleum ether solution to give 11 g of intermediate 3 as a white solid (60.7% yield).

Step 4:

In a dried 500 mL round bottom flask, intermediate 3 (9.60 g, 42.19 mmol), bis(pinacolato)diboron (13.93 g, 54.86 mmol), X-Phos (0.99 g, 2.10 mmol), palladium acetate (0.47 g, 2.10 mmol), potassium acetate (10.30 g, 105.00 mmol) and dioxane (200 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated at 100° C. and stirred overnight. After the reaction was completed, it was filtered through celite and anhydrous magnesium sulfate, and washed twice with ethyl acetate. The organic phase was collected and concentrated under reduced pressure to obtain a crude product, which was directly used in the next step.

Step 5:

In a dried 500 mL round bottom flask, intermediate 4 (crude product), 2-bromopyridine (6.23 g, 39.45 mmol), Pd(PPh₃)₄(2.07 g, 1.79 mmol), sodium carbonate (9.49 g, 89.50 mmol), dioxane (250 mL) and water (50 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated at 100° C. and reacted for 12 h. After the reaction was completed, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography by eluting with a gradient of PE:EA=10: 1 to 5:1 (v/v) to obtain 11.4 g of intermediate 5 as a white solid (98% yield). Intermediate 5 is Compound 1 corresponding to ligand L_(a), and the structure of the product was confirmed by NMR and GCMS.

Step 6:

In a dried 500 mL round bottom flask, intermediate 5 (3.52 g, 12.96 mmol), iridium complex (4.50 g, 6.31 mmol), and ethanol (250 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then heated to reflux for 24 h.

After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) as a yellow solid (1.5 g, 28.7% yield). The product was identified as the target product with a molecular weight of 770.

Synthesis Example 2: Synthesis of Compound IrL_(a4)(L_(b1))₂ (Metal Complex 4)

Step 1:

In a dried 500 mL round bottom flask, 6-chloro-dibenzofuran-1-nitrile (4.6 g, 20.2 mmol), bis(pinacolato)diboron (5.9 g, 23.2 mmol), palladium acetate (0.14 g, 0.6 mmol), potassium acetate (2.97 g, 30.3 mmol), X-Phos (0.58 g, 1.21 mmol) and 1,4-dioxane (90 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated to reflux and stirred overnight. After the reaction was completed, it was filtered through celite and anhydrous magnesium sulfate, and washed twice with ethyl acetate. The organic phase was collected and concentrated under reduced pressure to obtain intermediate 6, which was directly used in the next step.

Step 2:

In a dried 500 mL round bottom flask, intermediate 6 (6.4 g, 20.2 mmol), 2-bromopyridine (3.2 g, 20.2 mmol), Pd(PPh₃)₄(1.4 g, 1.2 mmol), potassium carbonate (4.2 g, 30.3 mmol), 1,4-dioxane (90 mL) and water (30 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated at 100° C. and reacted for 12 h. After the reaction was completed, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography by eluting with a gradient of PE:EA=20: 1 to 10:1 (v/v) to obtain 4 g of intermediate 7 as a white solid (74% yield). Intermediate 7 is compound 4 corresponding to ligand L_(a), and the structure of the product was confirmed by NMR and GCMS.

Step 3:

In a dried 500 mL round bottom flask, intermediate 7 (2.9 g, 11.0 mmol), iridium complex (4.0 g, 5.5 mmol), and ethanol (250 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then heated to reflux for 24 h.

After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a4)(L_(b1))₂ (Metal complex 4) as a yellow solid (1.5 g, 36% yield). The product structure was identified as the target product with a molecular weight of 770.

Synthesis Example 3: Synthesis of Compound IrL_(a2)(L_(b1))₂ (Metal Complex 2)

Step 1:

To a dried 1000 mL round bottom flask, 3-chloro-2-methoxyphenylboronic acid (12.00 g, 64.37 mmol), 2-fluoro-3-bromobenzonitrile (12.26 g, 61.31 mmol), tetrakis(triphenylphosphine)palladium (Pd(PPh₃)₄) (3.25 g, 3.05 mmol), potassium carbonate (18.61 g, 134.80 mmol), 1,4-dioxane (500 mL) and water (100 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, then it was heated in a heating mantle and stirred under reflux for 12 h. After the reaction was cooled, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography, eluting with 5% (v/v) ethyl acetate (EA)/petroleum ether (PE), to give 13.2 g of intermediate 8 as a white product (82.5% yield).

Step 2:

In a dried 500 mL three-necked flask, intermediate 8 (13.20 g, 50.50 mmol), and 350 mL of dichloromethane were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and stirred in an ice bath at 0° C. for 5 minutes. Boron tribromide (19.0 g, 75.74 mmol) was added dropwise slowly. After the completion of the addition, the reaction was warmed up to room temperature and stirred for 12 h. After the reaction was completed, the reaction was quenched with ice-water in an ice bath and neutralized with a saturated aqueous solution of sodium bicarbonate. A large amount of white solid product was precipitated, which was directly filtered, washed with water three times, and dried under reduced pressure to obtain 11.75 g of intermediate 9 as a white solid (94% yield).

Step 3:

In a dried 500 mL round-bottomed flask, intermediate 9 (11.75 g, 47.47 mmol), potassium carbonate (19.6 g, 142.4 mmol), and DMF (300 mL) were added successively. The mixture was then heated in a heating mantle at 100° C. and stirred for 12 h. After the reaction was completed, it was cooled and filtered through celite. The organic phase was washed with saturated brine, extracted twice with ethyl acetate, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography, eluting with a 20% (v/v) dichloromethane (DCM/petroleum ether(PE)) to give 7.09 g of intermediate 10 as a white solid (65.7% yield).

Step 4:

In a dried 500 mL round bottom flask, intermediate 10 (4.10 g, 18.02 mmol), bis(pinacolato)diboron (5.95 g, 23.42 mmol), X-Phos (0.43 g, 0.90 mmol), palladium acetate (0.20 g, 0.90 mmol), potassium acetate (4.46 g, 45.00 mmol) and dioxane (100 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated at 100° C. and stirred overnight. After the reaction was completed, it was filtered through celite and anhydrous magnesium sulfate, and washed twice with ethyl acetate. The organic phase was collected and concentrated under reduced pressure to obtain crude product intermediate 11, which was directly used in the next step.

Step 5:

In a dried 500 mL round bottom flask, intermediate 11 (crude product), 2-bromopyridine (2.66 g, 16.85 mmol), Pd(PPh₃)₄(0.88 g, 0.76 mmol), sodium carbonate (4.05 g, 38.25 mmol), dioxane (150 mL) and water (30 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, heated at 100° C. and reacted for 12 h. After the reaction was completed, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography by eluting with a gradient of PE:EA=10: 1 to 5:1 (v/v) to obtain 4.1 g of intermediate 12 as a white solid (90% yield). Intermediate 12 is compound 2 corresponding to ligand L_(a), and the structure of the product was confirmed by NMR and GCMS.

Step 6:

In a dried 500 mL round bottom flask, intermediate 12 (3.52 g, 12.96 mmol), iridium complex (4.50 g, 6.31 mmol), and ethanol (250 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then the reaction was heated to reflux for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the IrL_(a2)(L_(b1))₂ (Metal complex 2) as a yellow solid (1.3 g, 24.5% yield). The product structure was identified as the target product with a molecular weight of 770.

Synthesis Example 4: Synthesis of Compound IrL_(a3)(L_(b1))₂ (Metal Complex 3)

Step 1:

In a dried 500 mL round bottom flask, 6-chloro-dibenzofuran-2-nitrile (5 g, 22.0 mmol), bis(pinacolato)diboron (6.4 g, 25.3 mmol), X-Phos (0.6 g, 1.3 mmol), palladium acetate (0.15 g, 0.6 mmol), potassium acetate (3.2 g, 32.6 mmol) and dioxane (90 mL) were added successively. The reaction system was then replaced with N₂ three times and heated to reflux and stirred overnight under N₂ protection. After the reaction was completed, it was filtered through celite and anhydrous magnesium sulfate, and washed twice with ethyl acetate. The organic phase was collected and concentrated under reduced pressure to obtain intermediate 13, which was directly used in the next step.

Step 2:

In a dried 500 mL round bottom flask, intermediate 13 (crude product), 2-bromopyridine (3.5 g, 22.2 mmol), Pd(dppf)Cl₂ (0.48 g, 0.66 mmol), potassium carbonate (3.5 g, 25.3 mmol), dioxane (90 mL) and water (30 mL) were added successively. Under N₂ protection, the reaction was heated to reflux and reacted for 12 h. After the reaction was completed, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography to obtain 3.9 g of intermediate 14 as a white solid (65.6% yield), and the structure of the product was confirmed by NMR and GCMS.

Step 3:

In a dried 250 mL round bottom flask, intermediate 14 (3.5 g, 12.9 mmol), iridium complex (4.6 g, 6.3 mmol), 2-ethoxyethanol (50 mL) and DMF (50 mL) were added successively. Under N₂ protection, the mixture was heated to 85° C. and reacted for 96 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a3)(L_(b1))₂ (Metal complex 3) as a yellow solid (2.1 g, 43.3% yield). The product was identified as the target product with a molecular weight of 770.

Synthesis Example 5: Synthesis of Compound IrL_(a1)(L_(b3))₂ (Metal Complex 67)

Step 1:

In a dried 500 mL round bottom flask, intermediate 5 (2.4 g, 8.9 mmol), iridium complex (3.3 g, 4.4 mmol), and ethanol (250 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then the reaction was heated to reflux for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a1)(L_(b3))₂ (Metal complex 67) as a yellow solid (2.2 g, 63.7% yield). The product was identified as the target product with a molecular weight of 798.

Synthesis Example 6: Synthesis of Compound IrL_(a1)(L_(b4))₂ (Metal Complex 107)

Step 1:

In a dried 500 mL round bottom flask, intermediate 5 (2.2 g, 8.1 mmol), iridium complex (4.0 g, 5.4 mmol), and ethanol (120 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then the reaction was heated to reflux for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane.

The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a1)(L_(b4))₂ (Metal complex 107) as a yellow solid (0.8 g, 18.6% yield). The product was identified as the target product with a molecular weight of 798.

Synthesis Example 7: Synthesis of Compound IrL_(a1)(L_(b8))₂ (Metal Complex 147)

Step 1:

In a dried 500 mL round bottom flask, intermediate 5 (2.4 g, 8.9 mmol), iridium complex (3.3 g, 4.4 mmol), and ethanol (250 mL) were added successively. The reaction system was then replaced with N₂ three times and protected by N₂, and then the reaction was heated to reflux for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a1)(L_(b8))₂ (Metal complex 147) as a yellow solid (1.0 g, 27.5% yield). The product was identified as the target product with a molecular weight of 826.

Synthesis Example 8: Synthesis of Compound IrL_(a221)(L_(b1))₂ (Metal Complex 17)

Step 1:

In a dried 500 mL round bottom flask, intermediate 4 (7.0 g, 22.0 mmol), 4-methyl-2-bromopyridine (4.2 g, 24.4 mmol), Pd(dppf)Cl₂ (0.67 g, 0.9 mmol), potassium carbonate (6.4 g, 46.3 mmol), dioxane (90 mL) and water (30 mL) were added successively. Under N₂ protection, the reaction was heated to reflux and reacted for 12 h. After the reaction was completed, it was extracted with ethyl acetate, washed with saturated brine three times, dried over anhydrous magnesium sulfate, and concentrated under reduced pressure. The crude product was purified by column chromatography to obtain 3 g of intermediate 15 as a white solid (48.0% yield), and the structure of the product was confirmed by NMR and LCMS.

Step 2:

In a dried 250 mL round bottom flask, intermediate 15 (3 g, 10.5 mmol), iridium complex (3.5 g, 5 mmol), and ethanol (100 mL) were added successively. Under N₂ protection, the mixture was heated to reflux and reacted for 36 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a221)(L_(b1))₂ (Metal complex 17) as a yellow solid (1.4 g, 33.6% yield). The product was identified as the target product with a molecular weight of 784.

Synthesis Example 9: Synthesis of Compound IrL_(a962)(L_(b1))₂ (Metal Complex 53)

Step 1:

In a dried 250 mL round bottom flask, intermediate 16 (2.6 g, 9 mmol), iridium complex (3.6 g, 5 mmol), 2-ethoxyethanol (50 mL) and DMF (50 mL) were added successively. Under N₂ protection, the mixture was heated to 85° C. and reacted for 96 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a962)(L_(b1))₂ (Metal complex 53) as a yellow solid (1.3 g, 33.3% yield). The product was identified as the target product with a molecular weight of 787.

Synthesis Example 10: Synthesis of Compound IrL_(a962)(L_(b3))₂ (Metal Complex 93)

Step 1:

In a dried 250 mL round bottom flask, intermediate 16 (2.8 g, 9.7 mmol), iridium complex (4.0 g, 5.4 mmol), 2-ethoxyethanol (50 mL) and DMF (50 mL) were added successively. Under N₂ protection, the mixture was heated to 85° C. and reacted for 96 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a962)(L_(b3))₂ (Metal complex 93) as a yellow solid (0.85 g, 19.3% yield). The product was identified as the target product with a molecular weight of 815.

Synthesis Example 11: Synthesis of Compound IrL_(a293)(L_(b1))₂ (Metal Complex 19)

Step 1:

In a dried 250 mL round bottom flask, intermediate 17 (2.6 g, 7.5 mmol), iridium complex (2.2 g, 6.0 mmol), and ethanol (150 mL) were added successively. Under N₂ protection, the mixture was heated to reflux and reacted for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a293)(L_(b1))₂ (Metal complex 19) as a yellow solid (0.6 g, 12% yield). The product was identified as the target product with a molecular weight of 846.

Synthesis Example 12: Synthesis of Compound IrL_(a293)(L_(b3))₂ (Metal Complex 77)

Step 1:

In a dried 250 mL round bottom flask, intermediate 17 (2.6 g, 7.5 mmol), iridium complex (2.2 g, 6.0 mmol), and ethanol (150 mL) were added successively. Under N₂ protection, the mixture was heated to reflux and reacted for 24 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a293)(L_(b3))₂ (Metal complex 77) as a yellow solid (0.6 g, 12% yield). The product was identified as the target product with a molecular weight of 874.

Synthesis Example 13: Synthesis of Compound IrL_(a987)(L_(b3))₂ (Metal Complex 102)

Step 1:

In a dried 250 mL round bottom flask, intermediate 18 (3.0 g, 8.5 mmol), iridium complex (4.2 g, 5.7 mmol), 2-ethoxyethanol (100 mL) and DMF (100 mL) were added successively. Under N₂ protection, the mixture was heated to 85° C. and reacted for 96 h. After the reaction was cooled, it was filtered through celite. The mixture was washed twice with methanol and n-hexane. The yellow solid above the celite was dissolved in dichloromethane. The organic phase was collected, concentrated under reduced pressure, and purified by column chromatography to obtain the compound IrL_(a987)(L_(b3))₂ (Metal complex 102) as a yellow solid (0.9 g, 18.0% yield). The product was identified as the target product with a molecular weight of 879.

Those skilled in the art should know that the above preparation method is only an exemplary example, and those skilled in the art can obtain other compound structures of the present disclosure by improving it.

DEVICE EXAMPLE Example 1

Firstly, a glass substrate with a 120 nm-thick indium tin oxide (ITO) anode was cleaned, and then treated with oxygen plasma and UV ozone. After processing, the substrate was oven-dried in a glovebox to remove moisture. The substrate was then mounted on a substrate holder and loaded into a vacuum chamber. The organic layers specified below were deposited by thermal vacuum evaporation sequentially on the ITO anode at a rate of 0.2-2 angstroms per second under a vacuum degree of about 10⁻⁸ Torr. Compound H1 (100 Å) was used as a hole injection layer (HIL). Compound HT (350 Å) was used as a hole transporting layer (HTL). Compound H1 (50 Å) was used as an electron blocking layer (EBL). Then, the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure was doped in the host compounds H1 and H2 and used as a light-emitting layer (EML, 8:46:46, 400 Å). Compound H2 (100 Å) was used as a hole blocking layer (HBL). On the HBL, a mixture of Compound ET and 8-hydroxyquinolinolato-lithium (Liq) was deposited as an electron transporting layer (ETL, 40:60, 350 Å). Finally, 10 Å of Liq was deposited as an electron injection layer, and 1200 Å of Al was deposited as a cathode. The device was then transferred back to the glovebox and encapsulated with a glass lid and a moisture getter to complete the device.

Example 2

The implementation of Example 2 was the same as that of Example 1, except that the compound IrL_(a2)(L_(b1))₂ (Metal complex 2) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1.

Example 3

The implementation of Example 3 was the same as that of Example 1, except that the compound IrL_(a1)(L_(b3))₂ (Metal complex 67) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 4

The implementation of Example 4 was the same as that of Example 1, except that the compound IrL_(a1)(L_(b4))₂ (Metal complex 107) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 5

The implementation of Example 5 was the same as that of Example 1, except that the compound IrL_(a1)(L_(b8))₂ (Metal complex 147) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 6

The implementation of Example 6 was the same as that of Example 1, except that the compound IrL_(a962)(L_(b1))₂ (Metal complex 53) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 7

The implementation of Example 7 was the same as that of Example 1, except that the compound IrL_(a962)(L_(b3))₂ (Metal complex 93) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 8

The implementation of Example 8 was the same as that of Example 1, except that the compound IrL_(a293)(L_(b3))₂ (Metal complex 77) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Example 9

The implementation of Example 9 was the same as that of Example 1, except that the compound IrL_(a987)(L_(b3))₂ (Metal complex 102) of the present disclosure was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1, respectively.

Comparative Example 1

The implementation of Comparative Example 1 was the same as that of Example 1, except that the comparative compound 1 was used in the light-emitting layer instead of the compound IrL_(a1)(L_(b1))₂ (Metal complex 1) of the present disclosure in the Example 1.

For a layer with more than one materials being used, it was obtained by doping different compounds at the recorded weight ratios.

Part detailed device layer structures and thicknesses are shown in Table 1.

Table 1 The device structure of the device examples

TABLE 1 The device structure of the device examples Device ID HIL HTL EBL EML HBL ETL Example 1 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a1)(L_(b1))₂ (Metal (100 Å) (40:60) Complex 1) (46:46:8) (350 Å) (400 Å) Example 2 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a2)(L_(b1))₂ (Metal (100 Å) (40:60) Complex 2) (46:46:8) (350 Å) (400 Å) Example 3 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a1)(L_(b3))₂ (Metal (100 Å) (40:60) Complex 67) (46:46:8) (350 Å) (400 Å) Example 4 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a1)(L_(b4))₂ (Metal (100 Å) (40:60) Complex 107) (46:46:8) (350 Å) (400 Å) Example 5 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a1)(L_(b8))₂ (Metal (100 Å) (40:60) Complex 147) (46:46:8) (350 Å) (400 Å) Example 6 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a962)(L_(b1))₂ (Metal (100 Å) (40:60) Complex 53) (46:46:8) (350 Å) (400 Å) Example 7 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a962)(L_(b3))₂ (Metal (100 Å) (40:60) Complex 93) (46:46:8) (350 Å) (400 Å) Example 8 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a293)(L_(b3))₂ (Metal (100 Å) (40:60) Complex 77) (46:46:8) (350 Å) (400 Å) Example 9 Compound Compound Compound Compound Compound Compound HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:IrL_(a987)(L_(b3))₂ (Metal (100 Å) (40:60) Complex 102) (46:46:8) (350 Å) (400 Å) Comparative Compound Compound Compound Compound Compound Compound Example 1 HI HT H1 H1:Compound H2 ET:Liq (100 Å) (350 Å) (50 Å) H2:Comparative (100 Å) (40:60) compound 1 (46:46:8) (350 Å) (400 Å)

The structures of the materials used in the device are as follows:

The IVL and lifetime characteristics of the device were measured at different current densities and voltages. Table 2 shows the data about the external quantum efficiency (EQE), kmax, full width at half maximum (FWHM), voltage (V), and CIE measured at 1000 nits.

TABLE 2 Device data Device λmax FWHM Voltage number CIE (x, y) (nm) (nm) (V) EQE (%) Example 1 0.316, 0.645 523 53.9 2.76 23.62 Example 2 0.325, 0.644 526 42.5 2.76 24.81 Comparative 0.341, 0.630 528 59.3 2.98 22.52 Example 1

Table 3 shows the data about the external quantum efficiency (EQE), kmax, full width at half maximum (FWHM), voltage (V), and CIE of Examples 3 to 9 and Comparative Example 1 measured at 1000 nits. The lifetime (LT97) data of Examples 3 to 9 and Comparative Example 1 were tested at a constant current of 80 mA/cm².

TABLE 3 Device data Device λmax FWHM Voltage EQE LT97 number CIE (x, y) (nm) (nm) (V) (%) (h) Example 3 0.341, 0.631 527 57.8 2.67 23.65 17.9 Example 4 0.345, 0.628 528 58.5 2.72 23.26 21.9 Example 5 0.339, 0.632 527 57.9 2.83 24.15 20.7 Example 6 0.326, 0.639 525 55.0 2.70 23.52 23.7 Example 7 0.345, 0.628 528 57.3 2.67 23.27 20.7 Example 8 0.346, 0.632 531 37.8 2.64 26.23 15.0 Example 9 0.346, 0.631 531 41.1 2.67 25.93 17.2 Comparative 0.341, 0.630 528 59.3 2.98 22.52 15.0 Example 1

Discussion:

As can be seen from Table 2, the device examples with the compounds of the present disclosure show several advantages over the comparative compound. Compared to Comparative Compound 1, the compounds of the present disclosure unexpectedly showed many characteristics, for example, in Examples 1 and 2, high efficiency of 23.62% and 24.81% EQE were achieved, respectively, and the voltage was more than 0.2 V lower than that of Comparative Compound 1 which contained no cyano substitution, and there was no noticeable blue-shifted or red-shifted light emission. The most unexpected is that they had a very narrow peak width of emitted light. In particular, the full width at half maximum of Example 2 was only 42.5 nm, which was unprecedented in green phosphorescent devices. These advantages will greatly help to improve the level and color saturation of green light devices.

As can be seen from Table 3, the device examples with the compounds of the present disclosure show several advantages over the comparative compound. Compared to Comparative Example 1, Examples 3-7 showed a higher EQE (23.25%-24.15% vs. 22.52%), and the life time was significantly better than Comparative Example 1 (17.9 h-23.7 h vs. 15 h). The life time of Example 6 was nearly 60% higher than that of Comparative Example 1 (23.7 h vs. 15 h), and the voltage was more than 0.2 V-0.3 V lower than that of Comparative Example 1 which contained no cyano substitution.

Compared with Comparative Example 1, Example 8 and Example 9 showed much higher EQE (26.23%, 25.93% vs. 22.52%), and a voltage drop exceeding 0.3 V (2.64 V-2.67 V vs. 2.98 V). The life time of Example 9 was 14.67% higher than that of Comparative Example 1 (17.2 h vs. 15 h). The most unexpected is that they had a very narrow peak width of emitted light. In particular, the full width at half maximum of Example 8 was only 37.8 nm, which was unprecedented in green phosphorescent devices.

Example 8 and Example 9 are comparisons of hydrogen and deuterated compounds at corresponding substitution positions. Example 9 has a longer lifespan than Example 8 and proves the advantages of deuterated compounds in the present disclosure.

It should be understood that the various embodiments described herein are merely examples and are not intended to limit the scope of the present disclosure. Therefore, as will be apparent to those skilled in the art, the claimed disclosure may include variations from the specific and preferred embodiments described herein. Many of the materials and structures described herein may be replaced with other materials and structures without departing from the spirit of the disclosure. It should be understood that various theories as to why the present disclosure works are not intended to be limiting. 

What is claimed is:
 1. A metal complex comprising a ligand L_(a) represented by Formula 1:

wherein, Cy is any structure selected from the group consisting of:

R may represent mono-substitution, up to the maximum available multi-substitution, or no substitution; when more than one R exists in any structure, the R may be the same or different; X₁ to X₄ are each independently selected from C, CR_(x1) or N, and at least one of X₁ to X₄ is C which is connected to the Cy; when more than one of X₁ to X₄ is CR_(x1), the R_(x1) may be the same or different; X₅ to X₈ are each independently selected from CR_(x2) or N; when more than one of X₅ to X₈ is CR_(x2), the R_(x2) may be the same or different; X is selected from the group consisting of O, S, Se, NR_(x3), CR_(x4)R_(x5) and SiR_(x6)R_(x7); R, R_(x1), R_(x2), R_(x3), R_(x4), R_(x5), R_(x6) and R_(x7) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, wherein, at least one of R_(x1) and R_(x2) is present and is a cyano group; wherein, “#” represents a position at which the metal is connected, and “*” represents a position at which X₁, X₂, X₃ or X₄ is connected; any two adjacent substituents can optionally be joined to form a ring; X₁, X₂, X₃ or X₄ is connected to the metal through a metal-carbon bond or a metal-nitrogen bond.
 2. The metal complex according to claim 1, wherein the Cy is

R may represent mono-substitution, up to the maximum available multi-substitution, or no substitution; when more than one R exists in any structure, the R may be the same or different; R is each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, wherein, “#” represents a position at which the metal is connected, and “*” represents a position at which X₁, X₂, X₃ or X₄ is connected; any two adjacent substituents can optionally be joined to form a ring.
 3. The metal complex according to claim 1, wherein the metal complex has a general formula of M(L_(a))_(m)(L_(b))_(n)(L_(c))_(q), wherein L_(a) is a first ligand coordinated to the metal M, and the L_(b) and the L_(c) are a second ligand and a third ligand coordinated to the metal M, respectively, the L_(b) and the L_(c) may be the same or different; the L_(a), L_(b) and L_(c) can optionally be linked to form a multidentate ligand; wherein, m is 1, 2 or 3, n is 0, 1 or 2, q is 0, 1 or 2, and m+n+q is equal to the oxidation state of M; wherein, the metal M is selected from the group consisting of Cu, Ag, Au, Ru, Rh, Pd, Os, Ir, and Pt; wherein, L_(a) is independently selected from the group consisting of:

wherein, X is selected from the group consisting of O, S, Se, NR_(x3), CR_(x4)R_(x5) and SiR_(x6)R_(x7); R₁, R₂, R₃ and R₄ may represent mono-, di-, tri- or tetra-substitution, or no substitution; R₁, R₂, R₃, R₄, R_(x3), R_(x4), R_(x5), R_(x6) and R_(x7) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, wherein, at least one of R₃ and R₄ is present and is a cyano group; any two adjacent substituents can optionally be joined to form a ring; wherein, the L_(b) and L_(c) are each independently selected from the group consisting of:

wherein, R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or tetra-substitution, or no substitution; X_(b) is selected from the group consisting of: O, S, Se, NR_(N1), and CR_(C1)R_(C2); R_(a), R_(b), R_(c), R_(N1), R_(C1) and R_(C2) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof; and any two adjacent substituents can optionally be joined to form a ring.
 4. The metal complex according to claim 3, wherein, the metal M is selected from Pt, Os or Ir.
 5. The metal complex according to claim 3, wherein the metal complex has a structure represented by any one of Formulas 2 to 10:

wherein, m is 1, 2 or 3; X is selected from O, S or Se; R₁, R₃, and R₄ may represent mono-, di-, tri- or tetra-substitution, or no substitution; R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or tetra-substitution, or no substitution; R₁, R₃, R₄, R_(a), R_(b) and R_(c) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof; wherein, at least one of R₃ and R₄ is present and is a cyano group; any two adjacent substituents can optionally be joined to form a ring.
 6. The metal complex according to claim 5, wherein the metal complex has a structure of Formula 2-a:

wherein, m is 1, 2 or 3; X is selected from O, S or Se; R₃, and R₄ may represent mono-, di-, tri- or tetra-substitution, or no substitution; R_(a), R_(b), and R_(c) may represent mono-, di-, tri- or tetra-substitution, or no substitution; wherein, R₁₁, R₁₂, R₁₃, R₁₄, R₃, R₄, R_(a), and R_(b) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, wherein, at least one of R₃ and R₄ is present and is a cyano group; any two adjacent substituents can optionally be joined to form a ring.
 7. The metal complex according to claim 6, when R₁₁ and R₁₄ are both hydrogen, R₁₂ and R₁₃ are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof, and the sum of carbon atoms in R₁₂ and R₁₃ is less than or equal to 1; alternatively, when at least one of R₁₁ and R₁₄ is not hydrogen, R₁₂ and R₁₃ are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted heteroalkyl group having 1-20 carbon atoms, a substituted or unsubstituted arylalkyl group having 7-30 carbon atoms, a substituted or unsubstituted alkoxy group having 1-20 carbon atoms, a substituted or unsubstituted aryloxy group having 6-30 carbon atoms, a substituted or unsubstituted alkenyl group having 2-20 carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a substituted or unsubstituted arylsilyl group having 6-20 carbon atoms, a substituted or unsubstituted amino group having 0-20 carbon atoms, an acyl group, a carbonyl group, a carboxylic acid group, an ester group, a cyano group, an isocyano group, thioalkyl, sulfinyl, sulfonyl, phosphino, and combinations thereof.
 8. The metal complex according to claim 6, wherein, R₁₁, R₁₂, R₁₃, R₁₄, R_(a), and R_(b) are each independently selected from the group consisting of hydrogen, deuterium, halogen, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, and combinations thereof; wherein, R₃ and R₄ are each independently selected from the group consisting of hydrogen, deuterium, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a cyano group, and combinations thereof, wherein, at least one of R₃ and R₄ is present and is a cyano group.
 9. The metal complex according to claim 1, wherein at least one of X₅ to X₈ in Formula 1 is CR_(x2), and the R_(x2) is a cyano group.
 10. The metal complex according to claim 1, wherein X₅ to X₈ are each independently selected from CR_(x2), and at least one of R_(x2) is a cyano group.
 11. The metal complex according to claim 1, wherein X₇ is selected from CR_(x2), and the R_(x2) is a cyano group; or X₈ is selected from CR_(x2), and the R_(x2) is a cyano group.
 12. The metal complex according to claim 5, wherein R₄ may represent mono-, di-, tri- or tetra-substitution; when more than one R₄ exists, the R₄ may be the same or different; R₄ is selected from the group consisting of deuterium, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a cyano group, and combinations thereof, and at least one R₄ is a cyano group.
 13. The metal complex according to claim 5, wherein R₄ may represent mono-, di-, tri- or tetra-substitution; when more than one R₄ exists, the R₄ may be the same or different; R₄ is selected from the group consisting of deuterium, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, a substituted or unsubstituted aryl group having 6-30 carbon atoms, a substituted or unsubstituted heteroaryl group having 3-30 carbon atoms, a substituted or unsubstituted alkylsilyl group having 3-20 carbon atoms, a cyano group, and combinations thereof, and at least one R₄ is a cyano group; wherein R₃ may represent mono-, di-substitution, or no substitution; R₃ is selected from the group consisting of hydrogen, deuterium, a substituted or unsubstituted alkyl group having 1-20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3-20 ring carbon atoms, and combinations thereof.
 14. The metal complex according to claim 3, wherein the ligand L_(a) is selected from the group consisting of:


15. The metal complex according to claim 14, wherein the L_(a) can be partially or fully deuterated.
 16. The metal complex according to claim 14, wherein the hydrogen on the aryl group in L_(a) can be partially or fully deuterated; and/or wherein the hydrogen on the alkyl group in L_(a) can be partially or fully deuterated.
 17. The metal complex according to claim 14, wherein the metal complex has the Formula IrL_(a)(L_(b))₂ or Ir(L_(a))₂L_(b), wherein L_(a) is one or two selected from L_(a1) to L_(a1019), and L_(b) is one or two selected from the group consisting of:


18. The metal complex according to claim 17, wherein the metal complex has the Formula Ir(L_(a))₂L_(c) or IrL_(a)(L_(c))₂, wherein L_(a) is one or two selected from L_(a1) to L_(a1019), and L_(c) is one or two selected from the group consisting of:


19. The metal complex according to claim 18, wherein the metal complex has a structure represented by any one selected from the group consisting of Metal complex 1 to Metal complex 316: wherein, Metal complex 1 to Metal complex 226 have the structure of IrL_(a)(L_(b))₂, wherein two L_(b) are the same, wherein L_(a) and L_(b) correspond to the structures as shown in the following table, respectively: Metal Metal complex L_(a) L_(b) complex L_(a) L_(b) 1 L_(a1) L_(b1) 2 L_(a2) L_(b1) 3 L_(a3) L_(b1) 4 L_(a4) L_(b1) 5 L_(a121) L_(b1) 6 L_(a122) L_(b1) 7 L_(a123) L_(b1) 8 L_(a137) L_(b1) 9 L_(a138) L_(b1) 10 L_(a139) L_(b1) 11 L_(a153) L_(b1) 12 L_(a154) L_(b1) 13 L_(a155) L_(b1) 14 L_(a169) L_(b1) 15 L_(a170) L_(b1) 16 L_(a171) L_(b1) 17 L_(a221) L_(b1) 18 L_(a222) L_(b1) 19 L_(a293) L_(b1) 20 L_(a294) L_(b1) 21 L_(a295) L_(b1) 22 L_(a297) L_(b1) 23 L_(a298) L_(b1) 24 L_(a299) L_(b1) 25 L_(a313) L_(b1) 26 L_(a314) L_(b1) 27 L_(a415) L_(b1) 28 L_(a416) L_(b1) 29 L_(a467) L_(b1) 30 L_(a468) L_(b1) 31 L_(a487) L_(b1) 32 L_(a488) L_(b1) 33 L_(a507) L_(b1) 34 L_(a508) L_(b1) 35 L_(a516) L_(b1) 36 L_(a517) L_(b1) 37 L_(a527) L_(b1) 38 L_(a528) L_(b1) 39 L_(a547) L_(b1) 40 L_(a548) L_(b1) 41 L_(a576) L_(b1) 42 L_(a577) L_(b1) 43 L_(a592) L_(b1) 44 L_(a593) L_(b1) 45 L_(a640) L_(b1) 46 L_(a652) L_(b1) 47 L_(a692) L_(b1) 48 L_(a693) L_(b1) 49 L_(a704) L_(b1) 50 L_(a842) L_(b1) 51 L_(a854) L_(b1) 52 L_(a896) L_(b1) 53 L_(a962) L_(b1) 54 L_(a966) L_(b1) 55 L_(a970) L_(b1) 56 L_(a973) L_(b1) 57 L_(a974) L_(b1) 58 L_(a975) L_(b1) 59 L_(a976) L_(b1) 60 L_(a978) L_(b1) 61 L_(a985) L_(b1) 62 L_(a987) L_(b1) 63 L_(a988) L_(b1) 64 L_(a999) L_(b1) 65 L_(a1003) L_(b1) 66 L_(a1010) L_(b1) 67 L_(a1) L_(b3) 68 L_(a2) L_(b3) 69 L_(a3) L_(b3) 70 L_(a4) L_(b3) 71 L_(a121) L_(b3) 72 L_(a122) L_(b3) 73 L_(a123) L_(b3) 74 L_(a137) L_(b3) 75 L_(a138) L_(b3) 76 L_(a139) L_(b3) 77 L_(a293) L_(b3) 78 L_(a294) L_(b3) 79 L_(a297) L_(b3) 80 L_(a298) L_(b3) 81 L_(a576) L_(b3) 82 L_(a577) L_(b3) 83 L_(a592) L_(b3) 84 L_(a593) L_(b3) 85 L_(a640) L_(b3) 86 L_(a652) L_(b3) 87 L_(a692) L_(b3) 88 L_(a693) L_(b3) 89 L_(a704) L_(b3) 90 L_(a842) L_(b3) 91 L_(a854) L_(b3) 92 L_(a896) L_(b3) 93 L_(a962) L_(b3) 94 L_(a966) L_(b3) 95 L_(a970) L_(b3) 96 L_(a973) L_(b3) 97 L_(a974) L_(b3) 98 L_(a975) L_(b3) 99 L_(a976) L_(b3) 100 L_(a978) L_(b3) 101 L_(a985) L_(b3) 102 L_(a987) L_(b3) 103 L_(a988) L_(b3) 104 L_(a999) L_(b3) 105 L_(a1003) L_(b3) 106 L_(a1010) L_(b3) 107 L_(a1) L_(b) 108 L_(a2) L_(b4) 109 L_(a3) L_(b4) 110 L_(a4) L_(b4) 111 L_(a121) L_(b4) 112 L_(a122) L_(b4) 113 L_(a123) L_(b4) 114 L_(a137) L_(b4) 115 L_(a138) L_(b4) 116 L_(a139) L_(b4) 117 L_(a293) L_(b4) 118 L_(a294) L_(b4) 119 L_(a297) L_(b4) 120 L_(a298) L_(b4) 121 L_(a576) L_(b4) 122 L_(a577) L_(b4) 123 L_(a592) L_(b4) 124 L_(a593) L_(b4) 125 L_(a640) L_(b4) 126 L_(a652) L_(b4) 127 L_(a692) L_(b4) 128 L_(a693) L_(b4) 129 L_(a704) L_(b4) 130 L_(a842) L_(b4) 131 L_(a854) L_(b4) 132 L_(a896) L_(b4) 133 L_(a962) L_(b4) 134 L_(a966) L_(b4) 135 L_(a970) L_(b4) 136 L_(a973) L_(b4) 137 L_(a974) L_(b4) 138 L_(a975) L_(b4) 139 L_(a976) L_(b4) 140 L_(a978) L_(b4) 141 L_(a985) L_(b4) 142 L_(a987) L_(b4) 143 L_(a988) L_(b4) 144 L_(a999) L_(b4) 145 L_(a1003) L_(b4) 146 L_(a1010) L_(b4) 147 L_(a1) L_(b8) 148 L_(a2) L_(b8) 149 L_(a3) L_(b8) 150 L_(a4) L_(b8) 151 L_(a121) L_(b8) 152 L_(a122) L_(b8) 153 L_(a123) L_(b8) 154 L_(a137) L_(b8) 155 L_(a138) L_(b8) 156 L_(a139) L_(b8) 157 L_(a293) L_(b8) 158 L_(a294) L_(b8) 159 L_(a297) L_(b8) 160 L_(a298) L_(b8) 161 L_(a576) L_(b8) 162 L_(a577) L_(b8) 163 L_(a592) L_(b8) 164 L_(a593) L_(b8) 165 L_(a640) L_(b8) 166 L_(a652) L_(bs) 167 L_(a692) L_(b8) 168 L_(a693) L_(b8) 169 L_(a704) L_(b8) 170 L_(a842) L_(b8) 171 L_(a854) L_(b8) 172 L_(a896) L_(b8) 173 L_(a962) L_(b8) 174 L_(a966) L_(b8) 175 L_(a970) L_(b8) 176 L_(a973) L_(b8) 177 L_(a974) L_(b8) 178 L_(a975) L_(b8) 179 L_(a976) L_(b8) 180 L_(a978) L_(b8) 181 L_(a985) L_(b8) 182 L_(a987) L_(b8) 183 L_(a988) L_(b8) 184 L_(a999) L_(b8) 185 L_(a1003) L_(b8) 186 L_(a1010) L_(b8) 187 L_(a1) L_(b30) 188 L_(a2) L_(b30) 189 L_(a3) L_(b30) 190 L_(a4) L_(b30) 191 L_(a121) L_(b30) 192 L_(a122) L_(b30) 193 L_(a123) L_(b30) 194 L_(a137) L_(b30) 195 L_(a138) L_(b30) 196 L_(a139) L_(b30) 197 L_(a293) L_(b30) 198 L_(a294) L_(b30) 199 L_(a297) L_(b30) 200 L_(a298) L_(b30) 201 L_(a576) L_(b30) 202 L_(a577) L_(b30) 203 L_(a592) L_(b30) 204 L_(a593) L_(b30) 205 L_(a640) L_(b30) 206 L_(a652) L_(b30) 207 L_(a692) L_(b30) 208 L_(a693) L_(b30) 209 L_(a704) L_(b30) 210 L_(a842) L_(b30) 211 L_(a854) L_(b30) 212 L_(a896) L_(b30) 213 L_(a962) L_(b30) 214 L_(a966) L_(b30) 215 L_(a970) L_(b30) 216 L_(a973) L_(b30) 217 L_(a974) L_(b30) 218 L_(a975) L_(b30) 219 L_(a976) L_(b30) 220 L_(a978) L_(b30) 221 L_(a985) L_(b30) 222 L_(a987) L_(b30) 223 L_(a988) L_(b30) 224 L_(a999) L_(b30) 225 L_(a1003) L_(b30) 226 L_(a1010) L_(b30)

wherein, Metal complex 227 to Metal complex 274 have the structure of Ir(L_(a))₂L_(c), wherein two L_(a) are the same, wherein L_(a) and L_(c) correspond to the structures as shown in the following table, respectively: Metal Metal complex L_(a) L_(c) complex L_(a) L_(c) 227 L_(a323) L_(c1) 228 L_(a324) L_(c1) 229 L_(a328) L_(c1) 230 L_(a329) L_(c1) 231 L_(a333) L_(c1) 232 L_(a334) L_(c1) 233 L_(a338) L_(c1) 234 L_(a339) L_(c1) 235 L_(a343) L_(c1) 236 L_(a344) L_(c1) 237 L_(a348) L_(c1) 238 L_(a349) L_(c1) 239 L_(a353) L_(c1) 240 L_(a354) L_(c1) 241 L_(a358) L_(c1) 242 L_(a359) L_(c1) 243 L_(a363) L_(c1) 244 L_(a364) L_(c1) 245 L_(a368) L_(c1) 246 L_(a369) L_(c1) 247 L_(a373) L_(c1) 248 L_(a374) L_(c1) 249 L_(a388) L_(c1) 250 L_(a389) L_(c1) 251 L_(a323) L₃₁ 252 L_(a324) L₃₁ 253 L_(a328) L₃₁ 254 L_(a329) L₃₁ 255 L_(a333) L₃₁ 256 L_(a334) L₃₁ 257 L_(a338) L₃₁ 258 L_(a339) L₃₁ 259 L_(a343) L₃₁ 260 L_(a344) L₃₁ 261 L_(a348) L₃₁ 262 L_(a349) L₃₁ 263 L_(a353) L₃₁ 264 L_(a354) L₃₁ 265 L_(a358) L₃₁ 266 L_(a359) L₃₁ 267 L_(a363) L₃₁ 268 L_(a364) L₃₁ 269 L_(a368) L₃₁ 270 L_(a369) L₃₁ 271 L_(a373) L₃₁ 272 L_(a374) L₃₁ 273 L_(a388) L₃₁ 274 L_(a389) L₃₁

wherein, Metal complex 275 to Metal complex 316 have the structure of Ir(L_(a))₃, wherein three L_(a) are the same, wherein L_(a) corresponds to the structures as shown in the following table: Metal complex L_(a) 275 L_(a1) 276 L_(a2) 277 L_(a3) 278 L_(a121) 279 L_(a122) 280 L_(a137) 281 L_(a138) 282 L_(a293) 283 L_(a297) 284 L_(a298) 285 L_(a487) 286 L_(a488) 287 L_(a507) 288 L_(a508) 289 L_(a547) 290 L_(a548) 291 L_(a576) 292 L_(a577) 293 L_(a640) 294 L_(a641) 295 L_(a652) 296 L_(a653) 297 L_(a692) 298 L_(a693) 299 L_(a704) 300 L_(a842) 301 L_(a854) 302 L_(a896) 303 L_(a962) 304 L_(a966) 305 L_(a970) 306 L_(a973) 307 L_(a974) 308 L_(a975) 309 L_(a976) 310 L_(a978) 311 L_(a985) 312 L_(a987) 313 L_(a988) 314 L_(a999) 315 L_(a1003) 316 L_(a1010)


20. An electroluminescent device comprising: an anode, a cathode, and an organic layer disposed between the anode and the cathode, wherein the organic layer includes the metal complex according to claim
 1. 21. The electroluminescent device according to claim 20, wherein the organic layer is a light emitting layer, and the metal complex is a light emitting material.
 22. The electroluminescent device according to claim 21, wherein the organic layer further comprises a host material; or, wherein the organic layer contains at least two host materials.
 23. The electroluminescent device according to claim 22, wherein the host material comprises at least one chemical group selected from the group consisting of benzene, biphenyl, pyridine, pyrimidine, triazine, carbazole, azacarbazole, indolocarbazole, dibenzothiophene, azadibenzothiophen, dibenzofuran, azadibenzofuran, dibenzoselenophene, azadibenzoselenophene, triphenylene, azatriphenylene, fluorene, silicon-fluorene, naphthalene, quinoline, isoquinoline, quinazoline, quinoxaline, phenanthrene, azaphenanthrene, and combinations thereof.
 24. The electroluminescent device according to claim 20, wherein the electroluminescent device is incorporated into a device selected from the group consisting of a consumption product, an electronic component module, an organic light-emitting device and a lighting panel.
 25. A compound formulation comprising the metal complex according to claim
 1. 